AlZn4,5Mg1
(AZ5G)
No food using. |
| Mechanical characteristics:
Properties
|
Nominal chemical compound % (according to the standard EN 573-1) : |
|
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Others
|
Al
|
|
Each
|
Total
|
|
0,35
|
0,40
|
0,2
|
0,05-0,50
|
1,0-1,4
|
0,10-0,35
|
4,0-5,0
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Sheets
(according to the standard EN 485-2): |
| State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Rayon
de pliage |
Dureté HBS |
| Supérieur
à |
jusqu'à |
mini |
maxi |
mini |
maxi |
A
50 |
A |
180° |
90° |
| O |
>0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
- |
220
220
220
220 |
- |
140
140
140
140 |
12
13
15
12 |
- |
- |
- |
45
45
45
45 |
| T4
T
451 |
>
0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
320
320
320
320 |
- |
210
210
210
210 |
- |
- |
11
12
13
14 |
- |
2,0
e
2,5
e
3,5
e
5,0
e |
92
92
92
92 |
| |
>0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
350
350
350
350 |
- |
280
280
280
280 |
- |
- |
7
8
10
10 |
- |
|
104
104
104
104 |
| T651 |
12,5
40,0
100,0
150,0 |
40,0
100,0
150,0
175,0 |
350
340
330
330 |
- |
280
270
260
260 |
- |
- |
9
8
7
6 |
- |
- |
104
101
98
98 |
|
Top of the page
Sheets in
relief
(according to the standard EN 1386) : |
| State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Rayon
de pliage min recommandé à 90° |
| Sup
à |
Jusqu'à |
mini |
maxi |
Mini |
Maxi |
A
50 |
A |
|
O
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
-
-
-
-
|
220
220
220
220
|
-
-
-
-
|
140
140
140
140
|
6
8
10
12
|
-
-
-
12
|
3,0 t
3,0 t
3,0 t
-
|
|
T4
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
320
320
320
320
|
-
-
-
-
|
210
210
210
210
|
-
-
-
-
|
4
6
8
10
|
-
-
-
12
|
6,0 t
6,0 t
6,0 t
-
|
| T6 |
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
350
350
350
350
|
-
-
-
-
|
280
280
280
280
|
-
-
-
-
|
3
4
6
8
|
-
-
-
8
|
-
-
-
-
|
|
Top of the page
Extruded bars (according to the standard EN 755-2) : |
| State |
Sizes
mm |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| Diam
(D) |
size on flat or thickness (S) |
mini |
max |
mini |
max |
| T6 |
£
50
50<D£200
|
£
50
50<S£200
|
350
340
|
-
-
|
290
275
|
-
-
|
10
10
|
8
-
|
|
Top of the page
Extruded tubes (according to the standard EN-755-2) : |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
|
T6
|
£
15
|
350
|
-
|
290
|
-
|
10
|
8
|
|
Top of the page
Extruded sections (according to the standard EN-755-2) : |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
| T6 |
£
40
|
350
|
-
|
290
|
-
|
10
|
8
|
|
Top of the page
Drawn bars
(according to the standard EN-754-2) : |
| State |
Sizes
mm |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| Diam |
Plat |
mini |
max |
mini |
max |
| T6 |
|
|
|
- |
- |
|
|
|
|
Top of the page
Drawn tubes
(according to the standard EN-754-2) : |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
|
T6
|
20
|
350
|
-
|
280
|
|
10
|
8
|
|
Top of the page
Properties
(for information only): |
Corrosion : |
| General corrosion index |
Satisfactory
|
| Corrosion in industrial atmosphere |
Satisfactory
|
| Corrosion in sea atmosphere |
Satisfactory
|
| Corrosion in country atmosphere |
Good
|
| Corrosion under stress |
Good
|
| Exfoliation index |
Satisfactory
|
| Intercrystalline corrosion |
Good
|
| Tapping index |
Good
|
|
Top of the page
Anodizing: |
| Bright anodizing |
Not recommended
|
| Coloured anodizing |
Satisfactory
|
| Hard anodizing |
Good
|
| Protecting anodizing |
Good
|
|
Top of the page
Strain, workability: |
| |
Strain aging
|
| Cold working |
Not recommended
|
| Deep stamping |
Strongly inadvisable
|
| Strain by tension |
Not recommended
|
| Embossing ability |
Strongly inadvisable
|
| Extrusion ability |
Satisfactory
|
| Workability |
Very good
|
|
Top of the page
Welding: |
| Welding by electron beam |
Good
|
| Gas welding |
Good
|
| Arc welding |
Good
|
| Spot welding |
Good
|
| Brazing |
Satisfactory
|
| Soft brazing |
Satisfactory
|
|
Top of the page
Physical and elastic properties: |
| Elastic |
Physical |
| E |
G |
n |
Tsol |
Tliq |
Cp |
a |
r |
rel |
l |
EC |
| MPa |
MPa |
- |
°C |
°C |
J kg-1 K-1 |
µm m-1 K-1 |
kg m-3 |
nW
m |
W m-1 K-1 |
%IACS |
70000 |
26400 |
0.33 |
605 |
645 |
873 |
23.3 |
2780 |
49 |
140 |
35 |
|
| Legend: |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
| Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
| rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
| EC |
Electrical conductivity |
%IACS |
|
Top of the
page |