AlZn5,5MgCu
(AZ5GU)
No food using. |
| Mechanical characteristics:
Properties:
|
Nominal chemical compound % (according to the standard EN 573-1): |
|
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Ti
|
Others
|
Al
|
|
Each
|
Total
|
|
0,4
|
0,5
|
1,2-2,0
|
0,30
|
2,1-2,9
|
0,18-0,28
|
5,1-6,1
|
0,2
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Sheets
(according to the standard EN 485-2) : |
| State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Bending radius |
Hardness
HBS |
| More than |
until |
mini |
maxi |
mini |
maxi |
A
50 |
A |
180° |
90° |
| O |
>0,4
0,8
1,5
3,0
6,0
12,5 |
0,8
1,5
3,0
6,0
12,5
75,0 |
- |
275
275
275
275
275
275 |
- |
145
145
145
145
145
|
10
10
10
10
10
|
9 |
1,0
e
2,0
e
3,0
e
|
0,5
e
1,0
e
1,0
e
2,5
e
4,0
e
|
55
55
55
55
55
55 |
| T6
T 651
T62 |
>
0,4
0,8
1,5
3,0
6,0 |
0,8
1,5
3,0
6,0
12,5 |
525
540
540
545
540 |
- |
460
460
470
475
460 |
- |
|
- |
- |
4,5
e
5,5
e
6,5
e
8,0
e
12 e |
157
160
161
163
160 |
| |
12,5
25,0
50,0
60,0
80,0
90,0
100,0
120,0 |
25,0
50,0
60,0
80,0
90,0
100,0
120,0
150,0 |
540
530
525
495
490
460
410
360 |
- |
470
460
440
420
390
360
300
260 |
- |
- |
6
5
4
4
4
3
2
2 |
- |
- |
161
158
155
147
144
135
119
104 |
| T76
T7651 |
>1,5
3,0
6,0 |
3,0
6,0
12,5 |
500
500
490 |
- |
425
425
415 |
- |
7
8
7 |
- |
- |
- |
149
149
149 |
T73
T7351 |
>1,5
3,0
6,0 |
3,0
6,0
12,5 |
460
460
475 |
- |
385
385
390 |
- |
7
8
7 |
- |
- |
- |
137
137
140 |
| |
12,5
25,0
50,0
60,0
80,0 |
25,0
50,0
60,0
80,0
100,0 |
475
475
455
440
430 |
- |
390
390
360
340
340 |
- |
- |
6
5
5
5
5 |
- |
- |
140
140
133
129
126 |
|
Top of the page
Extruded bars (according to the standard EN 755-2) : |
| State |
Sizes
(mm) |
Rm
( MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
| Diam
|
mini |
maxi |
mini |
maxi |
mini |
mini |
| O/H111 |
<200 |
|
275 |
|
165 |
10 |
8 |
|
<25
25 à
100
100
à 150
150
à 200 |
540
560
530
470 |
- |
480
500
470
400 |
- |
7
7
6
5 |
5
|
| |
<25
25 à
75
75 à
100
100
à 150 |
485
475
470
440 |
- |
420
405
390
360 |
- |
7
7
6
6 |
5
|
|
Top of the page
Extruded tubes (according to the standard EN-755-2) : |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
| O/H111 |
£
10
|
-
|
275
|
-
|
165
|
10
|
-
|
|
T6/T6510/T6511
|
£
5
5<e£10
10<e£50
|
540
560
560
|
-
-
-
|
485
505
495
|
-
-
-
|
8
7
6
|
6
5
4
|
|
T73/T73510/T73511
|
£
5
5<e£25
25<e£50
|
470
485
475
|
-
-
-
|
400
420
405
|
-
-
-
|
7
8
8
|
5
6
|
|
Top of the page
Extruded sections (according to the standard EN 755-2) : |
State |
Sizes
|
Rm(
MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
mm |
mini |
mini |
mini |
mini |
T6/T6510/T6511 |
£
25
25<e£60
|
530
540
|
460
470
|
6
6
|
4
|
T73/T73510/T73511 |
£
25
|
485
|
420
|
7
|
5 |
|
Top of the page
Drawn bars
(according to the standard EN 754-2) : |
| State |
Sizes
(mm) |
Rm
( MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
| Diam
|
mini |
maxi |
mini |
maxi |
mini |
mini |
| O/H111 |
<80
|
- |
275 |
|
165 |
10 |
8 |
T6 |
<80 |
520 |
- |
460 |
- |
7 |
6 |
T651 |
<80 |
520 |
- |
460 |
- |
5 |
4 |
T73 |
<80
|
455 |
- |
385 |
- |
10 |
8 |
| T7351 |
<80 |
455 |
- |
385 |
- |
8 |
6 |
|
Top of the page
Drawn tubes
(according to the standard EN-754-2) : |
| State |
Sizes mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
| O/H111 |
£
20
|
-
|
275
|
-
|
165
|
10
|
8
|
|
T6
|
£
20
|
540
|
-
|
485
|
-
|
7
|
6
|
|
T6510/T6511
|
£
20
|
540
|
-
|
485
|
|
5
|
4
|
|
T73
|
£
20
|
455
|
-
|
385
|
-
|
10
|
8
|
|
T7310/T73511
|
£
20
|
455
|
-
|
385
|
-
|
8
|
6
|
|
Top of the page
Properties
(for information only): |
Corrosion : |
| General corrosion index |
Not recommended
|
| Corrosion in industrial atmosphere |
Not recommended
|
| Corrosion in sea atmosphere |
Not recommended
|
| Corrosion in country atmosphere |
Satisfactory
|
| Corrosion under stress |
Satisfactory
|
| Exfoliation index |
Not recommended
|
| Intercrystalline corrosion |
Satisfactory
|
| Tapping index |
Satisfactory
|
|
Top of the page
Anodizing: |
| Bright anodizing |
Not recommended
|
| Coloured anodizing |
Not recommended
|
| Hard anodizing |
Satisfactory
|
| Protecting anodizing |
Good
|
|
Top of the page
Strain, workability: |
| |
T6
|
| Cold working |
Not recommended
|
| Deep stamping |
Strongly inadvisable
|
| Strain by tension |
Not recommended
|
| Embossing ability |
Strongly inadvisable
|
| Extrusion ability |
Satisfactory
|
| Workability |
Très
bon
|
|
Top of the page
Welding: |
| Welding by electron beam |
Good
|
| Gas welding |
Not recommended
|
| Arc welding |
Not recommended
|
| Spot welding |
Good
|
| Brazing |
Not recommended
|
| Soft brazing |
Not recommended
|
|
| Top of the page
Physical and elastic properties: |
| State |
Elastic |
Physical |
|
|
E |
G |
n |
Tsol |
Tliq |
Cp |
a |
r |
rel |
l |
EC |
| MPa |
MPa |
- |
°C |
°C |
J kg-1 K-1 |
µm m-1 K-1 |
kg m-3 |
nW
m |
W m-1 K-1 |
%IACS |
| T6 |
72000 |
27100 |
0.33 |
475 |
635 |
862 |
23.5 |
2810 |
52 |
134 |
33 |
|
| Legend: |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
| Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
| rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
| EC |
Electrical conductivity |
%IACS |
|
Top of the page |