Chemical compound of rolled products (NFA 51-113) |
Agent: |
Cu |
Al |
Mn |
Ni |
Fe |
Pb |
Zn |
Sn |
Si |
P |
Misc. |
Mini
: |
reste |
8,2 |
- |
2 |
1,0 |
- |
- |
- |
- |
- |
- |
Maxi
: |
- |
10,2 |
1,5 |
4 |
3,0 |
0,05 |
0,3 |
0,2 |
0,15 |
- |
0,5 |
|
Mechanical characteristics of rolled products (NFA 51-113): |
State |
Max. thickness in mm |
Rm
in N/mm² mini |
Rp0,2
in N/mm² mini |
A%
mini |
Annealing |
100 |
500 |
180 |
25 |
|
Physical characteristics of rolled products (NFA 51-113): |
Mass volume in g/cm3 |
Coefficient
of linear expansion from 20 to 200 °C in K-1.10-6 |
Mass heat capacity at 20°C in J/kg.K |
Heat conductivity at 20°C in W/m.K |
Electrical resistivity at 20°C (annealing) in µOhm.cm |
Modulus of longitudinal elasticity in MPa |
7,67 |
17 |
418 |
139,2 |
16 |
125000 |
|
Chemical compound of wrought products (NFA 51-116) |
Agent: |
Cu |
Al |
Mn |
Ni |
Fe |
Pb |
Zn |
Sn |
Si |
P |
Misc. |
Mini
: |
reste |
8,4 |
- |
2 |
1 |
- |
- |
- |
- |
- |
- |
Maxi
: |
- |
10,1 |
1,5 |
4 |
3 |
0,05 |
0,3 |
0,1 |
0,1 |
- |
0,1 |
|
Mechanical characteristics of wrought products (NFA 51-116): |
State |
Section
S in mm² |
Min. mechanical characteristics |
Rm
in MPa |
Rp0,2
in MPa |
A% |
HBS |
KU
in J |
H3 |
less or equal to 490 |
640 |
280 |
15 |
165 |
12 |
from
490 to 2000 included |
640 |
270 |
16 |
160 |
12 |
from
2000 to 5000 included |
620 |
250 |
16 |
155 |
12 |
more than 5000 |
610 |
250 |
18 |
152 |
12 |
M2
or O |
|
500 |
180 |
25 |
115 |
25 |
|