Chemical compound of coppers and alloys according to the standard ASTM (USA):
Direct access by rubrics:
Rubrics ASTM :
Wrought pure coppers
Wrought alloyed coppers
Wrought brass
Wrought bronzes
Wrought cupro-aluminums
Wrought bronzes with silicon
Wrought complex brass
Wrought cupro-nickels
Cast pure coppers
Cast alloyed coppers
Cast brass
Cast bronzes with silicon
Cast special bronzes
Cast phosphorous bronzes
Cast cupro aluminums
Cast cupro-nickels
Cupro-plombs
Cast special alloys
Direct access by the alloy number:
Alloy number ASTM
C10100 to C12000
C12100 to C14181
C14200 to C15500
C15715 to C15815
C16200 to C18090
C18100 to C18835
C18900 to C19160
C19200 to C19900
C21000 to C28000
C31200 to C38500
C40400 to C48600
C50100 to C52480
C53400 to C54400
C60800 to C64210
C64700 to C66100
C66200 to C69750
C70100 to C72950
C73500 to C79860
C80100 to C81200
C81400 to C82800
C83300 to C83810
C84200 to C84800
C85200 to C85800
C86100 to C86800
C87300 to C87800
C89320 to C89940
C90200 to C91700
C92200 to C92900
C93100 to C94500
C94700 to C94900
C95200 to C95900
C96200 to C96950
C97300 to C97800
C98200 to C98840
C99300 to C99750
Wrought pure coppers: (See designation
of pure coppers according to the standard ISO )
Alloy number
Designation
Cu
Ag %
Troy
oz
As
Sb
P
Te
Other agents
(incl
Ag)
Min
Min
C10100(1)
OFE
99.99min(3)
--
--
0.0005
0.0004
0.0003
0.0002
0.0005
Oxygen (2)
C10200(1)
OF
99.95min(4)
--
--
--
--
--
--
0.0010
Oxygen
C10300
OFXLP
99.95min(5)
--
--
--
--
0.001-0.005
--
--
C10400(1)
OFS
99.95min(4)
0.027
8.0
--
--
--
--
0.0010
Oxygen
C10500(1)
OFS
99.95min(4)
0.034
10.0
--
--
--
--
0.0010
Oxygen
C10700(1)
OFS
99.95min(4)
0.085
25.0
--
--
--
--
0.0010
Oxygen
C10800
OFLP
99.95min(5)
--
--
--
--
0.005-0.012
--
--
C10910(1)
--
99.95min(4)
--
--
--
--
--
--
0.005
Oxygen
C10920
--
99.90min
--
--
--
--
--
--
0.02
Oxygen
C10930
--
99.90min
0.044
13.0
--
--
--
--
0.02
Oxygen
C10940
--
99.90min
0.085
25.0
--
--
--
--
0.02
Oxygen
C11000(1)
ETP
99.90min
--
--
--
--
--
--
(6)
C11010(1)
RHC
99.90min
--
--
--
--
--
--
(6)
C11020(1)
FRHC
99.90min
--
--
--
--
--
--
(6)
C11030(1)
CRTP
99.90min
--
--
--
--
--
--
(6)
C11040(1)
--
99.90min
--
--
0.0005
0.0004
--
0.0002
(7)
C11100(1)
ETP
99.90min
--
--
--
--
--
--
(8)
C11300(1)
STP
99.90min
0.027
8.0
--
--
--
--
(6)
C11400(1)
STP
99.90min
0.034
10.0
--
--
--
--
(6)
C11500(1)
STP
99.90min
0.054
16.0
--
--
--
--
(6)
C11600(1)
STP
99.90min
0.085
25.0
--
--
--
--
(6)
C11700
--
99.9min(9)
--
--
--
--
0.04
--
0.004-0.02
B
C12000
DLP
99.90min
--
--
--
--
0.004-0.012
--
--
(1)
: These are alloys with high conductibility of which the main characteristic is a minimum conductivity of 100% IACS (excepted C10100 of which the minimum is 101% IACS).
(2)
: The maximal limit of additionnal agents is: Bi, 1ppm (0.0001%) ;
Cd, 1ppm (0.0001%) ; Fe, 10ppm (0.0010%) ; Pb, 5ppm (0.0005%) ; Mn,
0.5ppm (0.00005%) ; Ni, 10ppm (0.0010%) ; Se, 3ppm (0.0003%) ; Ag, 25ppm(0.0025%) ;
S, 15ppm (0.0015%) ; Sn, 2ppm (0.0002%) ; Zn, 1ppm (0.0001%).
(3)
: The Cu content is obtained by subtracting all the impurities at 100%. That value excludes the Ag content. L
(4)
: The Cu content is obtained by subtracting all the impurities at 100%
(5)
: Includes P.
(6)
: The oxygen content and agents as marks can vary according to the obtention process.
(7)
: The maximal limit of additionnal agents is : Se, 2ppm (0.0002%) ;
Bi, 1.0ppm (0.00010%) ; Total :, Te + Se +Bi, 3ppm(0.0003%). Sn,
5ppm (0.0005%) ; Pb, 5ppm (0.0005%) ; Fe, 10ppm (0.0010%) ; Ni, 10ppm
(0.0010%), S, 15ppm (0.0015%) ; Ag, 25ppm (0.0025%) ; Oxygen,100-650ppm
(0.010-0.065%).
Le total maximum est de 65ppm(0.0065%) oxygène non inclus.
(8)
: Little quantities of Cd or other agents can be added on agreement, for reducing the softening at high temperature.
(9)
: Includes B + P.
Top of the page
Alloy number
Designation
Cu
Ag
%
Troy
oz
As
Sb
P
Te
Other agents
(incl
Ag)
Min
Min
C12100
DLPS
99.90min
0.014
4.0
--
--
0.005-0.012
--
--
C12200(1)
DHP
99.9min
--
--
--
--
0.015-0.040
--
--
C12210
--
99.90min
--
--
--
--
0.015-0.025
--
--
C12220
--
99.9min
--
--
--
--
0.040-0.065
--
--
C12300
DHPS
99.90min
--
--
--
--
0.015-0.040
--
--
C12500
FRTP
99.88min
--
--
0.012
0.003
--
0.025(2)
0.003
Bi
0.004
Pb
0.050
Ni
C12510
--
99.9min
--
--
--
0.003
0.03
0.025(2)
0.005
Bi
0.05
Fe
0.020
Pb
0.050
Ni
0.05
Sn
0.080
Zn
C12900
FRSTP
99.88min
0.054
16.0
0.012
0.003
--
0.025(3)
0.003
Bi
0.004
Pb
0.050
Ni
C13100
--
99.8min
--
--
--
--
--
--
--
C14180
--
99.90min
--
--
--
--
0.075
--
0.01
Al
0.02
Pb
C14181
--
99.90min
--
--
--
--
0.002
--
0.002
Cd
0.005
C
0.002
Pb
0.002
Zn
( 1)
: includes the desoxygenated copper containing some wastes of P
(2)
: 0.025 Te + Se.
(3)
: includes Te + Se.
Top of the page
Alloy number
Désignation
Cu
Ag
%
Troy
oz
As
Sb
P
Te
Other agents
(incl
Ag)
Min
Min
C14200
DPA
99.4min
--
--
0.15-.50
--
0.015-0.040
--
--
C14300
--
99.90min(1)
--
--
--
--
--
--
0.05-0.15
Cd
C14410
--
99.90min(2)
--
--
--
--
0.005-0.020
--
0.05
Fe
0.05
Pb
0.10-0.20
Sn
C14415
--
99.96min(2)
--
--
--
--
--
--
0.10-0.15
Sn
C14420
--
99.90min(3)
--
--
--
--
--
0.005-0.05
0.04-0.15
Sn
C14500(4)
PTE
99.90min(5)
--
--
--
--
0.004-0.012
0.40-0.7
--
C14510
--
99.85min(5)
--
--
--
--
0.010-0.030
0.30-0.7
0.05
Pb
C14520
DPTE
99.90min(5)
--
--
--
--
0.004-0.020
.40-.7
--
C14530
--
99.90min(2)
--
--
--
--
0.001-0.0010
0.003-0.023(6)
(6)
0.003-0.023
Sn
C14700(4)
--
90.90
min (7)
--
--
--
--
0.002-0.005(7)
--
(7)
0.20-0.50
S
C15000(8)
--
99.80min
--
--
--
--
--
--
0.10-0.20
Zr
C15100(8)
--
99.80min
--
--
--
--
--
--
0.05-0.15
Zr
C15150
--
99.90min
--
--
--
--
--
--
0.015-0.030
Zr
C15500
--
99.75min
0.027-0.10
8.0-30.0
--
--
0.040-0.080
--
0.08-0.13
Mg
(1)
: Includes Cd.
(2)
: Includes Cu + Ag + Sn.
(3)
: Includes Te + Sn.
(5)
: Includes Te.
(6)
: Includes Te + Se.
(7)
: Includes Cu + Ag + S + P.
(8)
: Cu + named agents, 99.9% min.
Top of the page
Alloy number
Designation
Cu
Al
Fe
Pb
Oxygen
Boron
Other agents
(incl
Ag)
C15715
--
99.62min
0.13-.017(1)
0.01
0.01
0.12-0.19(1)
--
--
C15720
--
99.52min
0.18-0.22(1)
0.01
0.01
0.16-0.24(1)
--
--
C15725
--
99.43min
0.23-0.27(1)
0.01
0.01
0.20-0.28(1)
--
--
C15760
--
98.77min
0.58-0.62(1)
0.01
0.01
0.52-0.59(1)
--
--
C15815
--
97.82min
0.130-.17(1)
0.01
0.01
0.19(1)
1.2-1.8
--
(1) : All the present aluminum is under the form of Al2O3 ; 0.04% of the present oxygen is under the form of Cu2O
haut
de page
Alloy number
Cu
Fe
Sn
Ni
Co
Cr
Si
Be
Pb
Other agents
(incl
Ag)
C16200(1)
Solde
0.02
--
--
--
--
--
--
--
0.7-1.2
Cd
C16500(1)
Solde
0.02
0.50-0.7
--
--
--
--
--
--
0.6-1.0
Cd
C17000(1)
Solde
--
--
--
0.20min(2)
--
0.20
1.60-1.79
--
0.20
Al
C17200(1)
Solde
--
--
--
0.20min(2)
--
0.20
1.80-2.00
--
0.20
Al
C17300(1)
Solde
--
--
--
0.20min(2)
--
0.20
1.80-2.00
0.20-0.6
0.20
Al
C17410(1)
Solde
0.20
--
--
0.35-0.6
--
0.20
0.15-0.50
--
0.20
Al
C17450(1)
Solde
0.20
0.25
0.50-1.0
--
--
0.20
0.150-0.50
--
0.20
Al
0.50
Zr
C17455(1)
Solde
0.20
0.25
0.50-1.0(3)
--
--
0.20
0.15-0.50
0.20-0.6
0.20
Al
0.50
Zr
C17460(1)
Solde
0.20
0.25
1.0-1.4
--
--
0.20
0.15-0.50
--
0.20
Al
0.50
Zr
C17465(1)
Solde
0.20
0.25
1.0-1.4(3)
--
--
0.20
0.15-0.50
0.20-0.6
0.20
Al
0.50
Zr
C17500(1)
Solde
0.10
--
--
2.4-2.7
--
0.20
0.4-0.7
--
0.20
Al
C17510(1)
Solde
0.10
--
1.4-2.2
0.3
--
0.20
0.2-0.6
--
0.20
Al
C17530(1)
Solde
0.20
--
1.8-2.5(3)
--
--
0.20
0.20-0.40
--
0.6
Al
C18000(1) (1)
Solde
0.15
--
1.8-3.0(4)
--
0.10-0.8
0.40-0.8
--
--
--
C18030(5)
Solde
--
0.08-.12
--
--
0.10-0.20
--
--
--
0.005-0.015
P
C18040(6)
Solde
--
0.20-0.30
--
--
0.25-0.35
--
--
--
0.005-0.015
P
0.05-0.15
Zn
C18045(5)
99.1min
--
0.20-0.30
--
--
0.20-0.35
0.05
--
--
0.15-0.30
Zn
C18050(7)
Solde
--
--
--
--
0.05-0.15
--
--
--
0.005-0.015
Te
C18070(7)
99.0min
--
--
--
--
0.15-0.40
0.02-0.07
--
--
0.01-0.40
Ti
C18080(7)
Solde
0.02-0.20
--
--
--
0.20-0.7
0.01-0.10
--
--
0.01-0.30
Ag
0.01-0.15
Ti
C18090(8)
96.0min
--
0.50-1.2
0.30-1.2
--
0.20-1.0
--
--
--
0.15-0.8
Ti
(1)
: Cu + named agents, 99.5% min.
(2)
: Ni + Co, .20% min.: Ni + Fe + Co, .6% max. Ni +
(3)
: The Ni value includes Co.
(4)
: Includes Co.
(5)
: Cu + named agents, 99.9% min.
(7)
: Cu + named agents, 99.8% min.
(8)
: Cu + named agents, 99.85% min.
Top of the page
Wrought lowly alloyed coppers:
Alloy number
Cu
(incl Ag)
Fe
Sn
Ni
Co
Cr
Si
Be
Pb
Other agents
C18100(1)
98.7min
--
--
--
--
0.40-1.2
--
--
--
0.03-0.06
Mg
0.08-0.20
Zr
C18135(1)
Solde
--
--
--
--
0.20-0.6
--
--
--
0.20-0.6
Cd
C18140(1)
Solde
--
--
--
--
0.15-0.45
0.005-0.05
--
--
0.05-0.25
Zr
C18145(1)
Solde
--
--
--
--
0.10-0.30
--
--
--
0.10-0.30
Zn
0.05-0.15
Zr
C18150(2)
Solde
--
--
--
--
0.50-1.5
--
--
--
0.05-0.25
Zr
C18200(1)
Solde
0.10
--
--
--
0.6-1.2
0.10
--
0.05
--
C18400(1)
Solde
0.15
--
--
--
0.40-1.2
0.10
--
--
0.005
As
0.005
Ca
0.05
Li
0.05
P
0.7
Zn
C18600(1)
Solde
0.25-0.8
--
0.25
0.10
0.10-1.0
--
--
--
0.05-0.50
Ti
0.05-0.40
Zr
C18610(1)
Solde
0.10
--
0.25
0.25-0.8
0.10-1.0
--
--
--
0.05-0.50
Ti
0.05-0.40
Zr
C18661(1)
Solde
0.10
0.20
--
--
--
--
--
--
0.10-0.7
Mg
0.001-0.02
P
C18665
99.0min
--
--
--
--
--
--
--
--
0.40-0.9
Mg
0.002-0.04
P
C18700
99.5min(3)
--
--
--
--
--
--
--
0.8-1.5
--
C18835
99.0min(1)
0.10
0.15-0.55
--
--
--
--
--
0.05
0.01
P
0.30
Zn
(1) : Cu + named agents, 99.5% min.
(2) : Cu + named agents, 99.7% min.
(3) : Includes Pb.
Top of the page
Alloy number
Cu
Fe
Sn
Ni
Co
Cr
Si
Be
Pb
Other agents
(incl
Ag)
C18900(1)
Solde
--
0.6-0.9
--
--
--
0.15-0.40
--
0.02
0.01
Al
0.10-0.30
Mn
0.05
P
0.10
Zn
C18980(1)
98.0min
--
1.0
--
--
--
0.50
--
0.02
0.50
Mn
0.15
P
C18990(2)
Solde
--
1.8-2.2
--
--
0.10-0.20
--
--
--
0.005-0.015
P
C19000(1)
Solde
0.10
--
0.9-1.3
--
--
--
--
0.05
0.15-0.35
P
0.8
Zn
C19010(1)
Solde
--
--
0.8-1.8
--
--
0.15-0.35
--
--
0.01-0.05
P
C19015(3)
Solde
--
--
0.50-2.4
--
--
0.10-0.40
--
--
0.02-0.15
Mg
0.02-0.20
P
C19020(3)
Solde
--
0.30-0.9
0.50-3.0
--
--
--
--
--
0.01-0.20
P
C19025(4)
Solde
0.10
0.7-1.1
0.8-1.2
--
--
--
--
--
0.03-0.07
P
0.20
Zn
C19030(4)
Solde
0.10
1.0-1.5
1.5-2.0
--
--
--
--
0.02
0.01-0.03
P
C19100(1)
Solde
0.20
--
0.9-1.3
--
--
--
--
0.10
0.15-0.35
P
0.35-0.6
Te
0.50
Zn
C19140(1)
Solde
0.05
0.05
0.8-1.2
--
--
--
--
0.40-0.8
0.15-0.35
P
0.50
Zn
C19150(1)
Solde
0.05
0.05
0.8-1.2
--
--
--
--
0.50-1.0
0.15-0.35
P
C19160(1)
Solde
0.05
0.05
0.8-1.2
--
--
--
--
0.8-1.2
0.15-0.35
P
0.50
Zn
(1) : Cu + named agents, 99.5% min.
(2) : Cu + named agents, 99.9% min.
(3)
: Cu + named agents, 99.8% min.
(4) : Cu + named agents, 99.7% min.
Top ot the page
Alloy number
Cu
Fe
Sn
Zn
Al
Pb
P
Other agents
C19200(1)
98.5min
0.8-1.2
--
0.20
--
--
0.01-0.04
--
C19210(1)
Solde
0.05-0.15
--
--
--
--
0.025-0.04
--
C19215(1)
Solde
0.05-0.20
--
1.1-3.5
--
--
0.025-0.050
--
C19220(1)
Solde
0.10-0.30
0.05-0.10
--
--
--
0.03-0.07
0.005-0.015
B
0.10-0.25
Ni
C19260(2)
98.5min
0.40-0.8
--
--
--
--
--
0.02-0.15
Mg
0.20-0.40
Ti
C19280(1)
Solde
0.50-1.5
0.30-0.7
0.30-0.7
--
--
0.005-0.015
--
C19400
97.0min
2.1-2.6
--
0.05-0.20
--
0.03
0.015-0.15
--
C19410(1)
Solde
1.8-2.3
0.6-0.9
0.10-0.20
--
--
0.015-0.050
--
C19450(1)
Solde
1.5-3.0
0.8-2.5
--
--
--
0.005-0.05
--
C19500(1)
96.0min
1.0-2.0
0.10-1.0
0.20
0.02
0.02
0.01-0.35
0.30-1.3
Co
C19520(1)
96.6min
0.50-1.5
--
--
--
0.01-3.5
--
--
C19700(1)
Solde
0.30-1.2
0.20
0.20
--
0.05
0.10-0.40
0.05
Co
0.01-0.20
Mg
0.05
Mn
0.05
Ni
C19710(3)
Solde
0.05-0.40
0.20
0.20
--
0.05
0.07-0.15
0.03-0.06
Mg
0.05
Mn
0.10
Ni(4)
C19720(3)
Solde
0.05-0.50
0.20
0.20
--
0.05
.05-.15
0.06-0.20
Mg
0.05
Mn
0.10
Ni(4)
C19750(1)
Solde
0.35-1.2
0.05-0.40
0.20
--
0.05
0.10-0.40
0.05
Co
0.01-0.20
Mg
0.05
Mn
0.05
Ni
C19800(1)
Solde
0.02-0.50
0.10-1.0
0.30-1.5
--
--
0.01-0.10
0.10-1.0
Mg
C19810(1)
Solde
1.5-3.0
--
1.0-5.0
--
--
0.10
0.10
Cr
0.10
Mg
0.10
Ti
0.10
Zr
C19900(3)
Solde
--
--
--
--
--
--
2.9-3.4
Ti
(1) : Cu + named agents,
99.8% min.
(2) : Cu + named agents,
99.9% min.
(3) : Cu + named agents,
99.5% min.
(4) : the Ni value includes Co.
Top of the page
Wrought brasses:
Alloy number
Cu
Pb
Fe
Zn
Other agents
C21000(1)
94.0-96.0
0.03(2)
0.05
Solde
--
C22000(1)
89.0-91.0
0.05
0.05
Solde
--
C22600(1)
86.0-89.0
0.05
0.05
Solde
--
C23000(1)
84.0-86.0
0.05
0.05
Solde
--
C23030(1)
83.5-85.5
0.05
0.05
Solde
0.20-0.40
Si
C23400(1)
81.0-84.0
0.05
0.05
Solde
--
C24000(1)
78.5-81.5
0.05
0.05
Solde
--
C24080(1)
78.0-82.0
0.20
--
Solde
0.10
Al
C25600(3)
71.0-73.0
0.05
0.05
Solde
--
C26000(3)
68.5-71.5
0.07
0.05
Solde
--
C26130(3)
68.5-71.5
0.05
0.05
Solde
0.02-0.08
As
C26200(3)
67.0-70.0
0.07
0.05
Solde
--
C26800(3)
64.0-68.5
0.15
0.05
Solde
--
C27000(3)
63.0-68.5
0.10
0.07
Solde
--
C27200(3)
62.0-65.0
0.07
0.07
Solde
--
C27400(3)
61.0-64.0
0.10
0.05
Solde
--
C28000(3)
59.0-63.0
0.30
0.07
Solde
--
(1)
: Cu + named agents, 99.8% min.
(2)
:0.05% Pb, max.for rounds, wires and tubes
(3)
: Cu + named agents, 99.7% min.
Top of the page
Alloy number
Cu
Pb
Fe
Zn
Other agents
C31200(1)
87.5-90.5
0.7-1.2
0.10
Solde
0.25
Ni
C31400(1)
87.5-90.5
1.3-2.5
0.10
Solde
0.7
Ni
C31600(1)
87.5-90.5
1.3-2.5
0.10
Solde
0.7-1.2
Ni
0.04-0.10
P
C32000(1)
83.5-86.5
1.5-2.2
0.10
Solde
0.25
Ni
C33000(1)
65.0-68.0
0.25-0.7
0.07
Solde
--
C33200(1)
65.0-68.0
1.5-2.5
0.07
Solde
--
C33500(1)
62.0-65.0
0.25-0.7
0.15(2)
Solde
--
C34000(1)
62.0-65.0
0.8-1.5
0.15(2)
Solde
--
C34200(1)
62.0-65.0
1.5-2.5
0.15(2)
Solde
--
C34500(1)
62.0-65.0
1.5-2.5
0.15
Solde
--
C35000(1)
60.0-63.0(3)
0.8-2.0
0.15(2)
Solde
--
C35300(4)
60.0-63.0(3)
1.5-2.5
0.15(2)
Solde
--
C35330(4)
59.5-64.0
1.5-3.5(5)
--
Solde
0.020-.25
As
C35600(4)
60.0-63.0
2.0-3.0
0.15(2)
Solde
--
C36000(4)
60.0-63.0
2.5-3.7
0.35
Solde
--
C36500(1)
58.0-61.0
0.25-0.7
0.15
Solde
0.25
Sn
C37000(1)
59.0-62.0
0.8-1.5
0.15
Solde
--
C37100(1)
58.0-62.0
0.6-1.2
0.15
Solde
--
C37700(4)
58.0-61.0
1.5-2.5
0.30
Solde
--
C37710(4)
56.5-60.0
1.0-3.0
0.30
Solde
--
C38000(4)
55.0-60.0
1.5-2.5
0.35
Solde
0.50
Al
0.30
Sn
C38500(4)
55.0-59.0
2.5-3.5
0.35
Solde
--
(1) : Cu + named agents,
99.6% min.
(2) : For the flat products, the rate of Fe is 0.10% max.
(3) : Cu, 61.0% min. for the rounds
(4) : Cu + named agents,
99.5% min.
(5) : Pb can be reduced at 1.0%
Top of the page
Alloy number
Cu
Pb
Fe
Sn
Zn
P
Other agents
C40400(1)
Solde
--
--
0.35-0.7
2.0-3.0
--
--
C40500(1)
94.0-96.0
0.05
0.05
0.7-1.3
Solde
--
--
C40810(1)
94.5-96.5
0.05
0.08-0.12
1.8-2.2
Solde
0.028-0.04
0.11-0.20
Ni
C40820(2)
94.0min
0.02
--
1.0-2.5
0.20-2.5
0.05
0.10-0.50
Ni
C40850(1)
94.5-96.5
0.05
0.05-0.20
2.6-4.0
Solde
0.01-0.20
0.05-0.20
Ni
C40860(1)
94.0-96.0
0.05
0.01-0.05
1.7-2.3
Solde
0.02-0.04
0.05-0.20
Ni
C41000(1)
91.0-93.0
0.05
0.05
2.0-2.8
Solde
--
--
C41100(1)
89.0-92.0
0.10
0.05
0.30-0.7
Solde
--
--
C41120(1)
89.0-92.0
0.05
0.05-0.20
0.30-0.7
Solde
0.01-0.35
0.05-0.20
Ni
C41300(1)
89.0-93.0
0.10
0.05
0.7-1.3
Solde
--
--
C41500(1)
89.0-93.0
0.10
0.05
1.5-2.2
Solde
--
--
C42000(1)
88.0-91.0
--
--
1.5-2.0
Solde
0.25
--
C42200(1)
86.0-89.0
0.05
0.05
0.8-1.4
Solde
0.35
--
C42220(1)
88.0-91.0
0.05
0.050-.20
0.7-1.4
Solde
0.020-.05
0.05-0.20
Ni
C42500(1)
87.0-90.0
0.05
0.05
1.5-3.0
Solde
0.35
--
C42520(1)
88.0-91.0
0.05
0.05-0.20
1.5-3.0
Solde
0.01-0.20
0.05-0.20
Ni
C42600(1)
87.0-90.0
0.05
0.05-0.20
2.5-4.0
Solde
0.01-0.20
0.05-0.20
Ni(3)
C43000(1)
84.0-87.0
0.10
0.05
1.7-2.7
Solde
--
--
C43400(1)
84.0-87.0
0.05
0.05
0.40-1.0
Solde
--
--
C43500(1)
79.0-83.0
0.10
0.05
0.6-1.2
Solde
--
--
C43600(1)
80.0-83.0
0.05
0.05
0.20-0.50
Solde
--
--
C44250(4)
73.0-76.0
0.07
0.20
0.50-1.5
Solde
0.10
0.20
Ni
C44300(4)
70.0-73.0
0.07
0.06
0.8-1.2(5)
Solde
--
0.02-0.06
As
C44400(4)
70.0-73.0
0.07
0.06
0.8-1.2(5)
Solde
--
0.02-0.10
Sb
C44500(4)
70.0-73.0
0.07
0.06
0.8-1.2(5)
Solde
0.02-0.10
--
C46200(4)
62.0-65.0
0.20
0.10
0.50-1.0
Solde
--
--
C46400(4)
59.0-62.0
0.20
0.10
0.50-1.0
Solde
--
--
C46500(4)
59.0-62.0
0.20
0.10
0.50-1.0
Solde
--
0.02-0.06
As
C47000(4)
57.0-61.0
0.05
--
0.25-1.0
Solde
--
0.01
Al
C47940(4)
63.0-66.0
1.0-2.0
0.10-1.0
1.2-2.0
Solde
--
0.10-0.50
Ni(3)
C48200(4)
59.0-62.0
0.40-1.0
0.10
0.50-1.0
Solde
--
--
C48500(4)
59.0-62.0
1.3-2.2
0.10
0.50-1.0
Solde
--
--
C48600(4)
59.0-62.0
1.0-2.5
--
0.30-1.5
Solde
--
0.02-0.25
As
(1) : Cu + named agents,
99.7% min.
(2) : Cu + named agents,
99.5% min.
(3) : The Ni value includes Co
(4) : Cu + named agents,
99.6% min.
(5) : For the cored products, the minimum Sn content is t 0.9%
Top of the page
Wrought bronzes:
Alloy number
Cu
Pb
Fe
Sn
Zn
P
Other agents
C50100(1)
Solde
0.05
0.05
0.50-0.8
--
0.01-0.05
--
C50200(1)
Solde
0.05
0.10
1.0-1.5
--
0.04
--
C50500(1)
Solde
0.05
0.10
1.0-1.7
0.30
0.03-0.35
--
C50510(2)
Solde
--
--
1.0-1.5
0.10-0.25
0.020-.07
0.15-0.40
Ni
C50580(1)
Solde
0.05
0.05-0.20
1.0-1.7
0.30
0.01-0.35
0.05-0.20
Ni
C50590(1)
97.0min
0.02
0.05-0.40
0.50-1.5
0.50
0.02-0.15
--
C50700(1)
Solde
0.05
0.10
1.5-2.0
--
0.30
--
C50705(1)
96.5min
0.02
0.10-0.40
1.5-2.0
0.50
0.04-0.15
--
C50710(1)
Solde
--
--
1.7-2.3
--
0.15
0.10-0.40
Ni
C50715(3)
Solde
0.02
0.05-0.15
1.7-2.3
--
0.025-0.04
--
C50725(1)
94.0min
0.02
0.05-0.20
1.5-2.5
1.5-3.0
0.02-0.06
--
C50780(1)
Solde
0.05
0.05-0.20
1.7-2.3
0.30
0.01-0.35
0.05-0.20
Ni
C50900(1)
Solde
0.05
0.10
2.5-3.8
0.30
0.03-0.30
--
C51000(1)
Solde
0.05
0.10
4.2-5.8
0.30
0.03-0.35
--
C51080(1)
Solde
0.05
0.05-0.20
4.8-5.8
0.30
0.01-0.35
0.05-0.20
Ni
C51100(1)
Solde
0.05
0.10
3.5-4.9
0.30
0.03-0.35
--
C51180(1)
Solde
0.05
0.050-.20
3.5-4.9
0.30
0.01-0.35
0.05-0.20
Ni
C51190(1)
Solde
0.02
0.05-0.15
3.0-6.5
--
0.025-0.045
0.15
Co
C51800(1)
Solde
0.02
--
4.0-6.0
--
0.10-0.35
0.01
Al
C51900(1)
Solde
0.05
0.10
5.0-7.0
0.30
0.03-0.35
--
C51980(1)
Solde
0.05
0.05-0.20
5.5-7.0
0.30
0.01-0.35
0.05-0.20
Ni
C52100(1)
Solde
0.05
0.10
7.0-9.0
0.20
0.03-0.35
--
C52180(1)
Solde
0.05
0.05-0.20
7.0-9.0
0.30
0.01-0.35
0.05-0.20
Ni
C52400(1)
Solde
0.05
0.10
9.0-11.0
0.20
0.03-0.35
--
C52480(1)
Solde
0.05
0.05-0.20
9.0-11.0
0.30
0.01-0.35
0.05-0.20
Ni
(1) : Cu + named agents,
99.5% min.
(2) : Cu + named agents,
99.7% min.
(3) : Cu + Sn + Fe + P, 99.5% min
Top of the page
Alloy number
Cu
Pb
Fe
Sn
Zn
P
Other agents
C53400(1)
Solde
0.8-1.2
0.10
3.5-5.8
0.30
0.03-0.35
--
C53800(2)
Solde
0.40-0.6
0.030
13.1-13.9
0.12
--
0.06
Mn
0.03
Ni(3)
C54400(1)
Solde
3.5-4.5
0.10
3.5-4.5
1.5-4.5
0.01-0.50
--
(1) : Cu + named agents,
99.5% min.
(2) : Cu + named agents,
99.8% min.
(3) : The Ni value includes Co.
Top of the page
Wrought cupro-aluminums:
Alloy number
Cu
Pb
Fe
Sn
Zn
Al
Mn
Si
Ni
Other agents
(incl
Ag)
C60800(1)
Solde
0.10
0.10
--
--
5.0-6.5
--
--
--
0.02-0.35
As
C61000(1)
Solde
0.02
0.50
--
0.20
6.0-8.5
--
0.10
--
--
C61300(2)
Solde
0.01
2.0-3.0
0.20-0.50
0.10(3)
6.0-7.5
0.20
0.10
0.15(4)
(3)
0.015
P
C61400(1)
Solde
0.01
1.5-3.5
--
0.20
6.0-8.0
1.0
--
--
0.015
P
C61500(1)
Solde
0.015
--
--
--
7.7-8.3
--
--
1.8-2.2(4)
--
C61550(1)
Solde
0.05
0.20
0.05
--
5.5-6.5
1.0
--
1.5-2.5(4)
--
C61800(1)
Solde
0.02
0.50-1.5
--
0.02
8.5-11.0
--
0.10
--
--
C61900(1)
Solde
0.02
3.0-4.5
0.6
0.8
8.5-10.0
--
--
--
--
C62200(1)
Solde
0.02
3.0-4.2
--
0.02
11.0-12.0
--
0.10
--
--
C62300(1)
Solde
--
2.0-4.0
0.6
--
8.5-10.0
0.50
0.25
1.0(4)
--
C62400(1)
Solde
--
2.0-4.5
0.20
--
10.0-11.5
0.30
0.25
--
--
C62500(1)
Solde
--
3.5-5.5
--
--
12.5-13.5
2.0
--
--
--
C62580(1)
Solde
0.02
3.0-5.0
--
0.02
12.0-13.0
--
0.04
--
--
C62581(1)
Solde
0.02
3.0-5.0
--
0.02
13.0-14.0
--
0.04
--
--
C62582(1)
Solde
0.02
3.0-5.0
--
0.20
14.0-15.0
--
0.04
--
--
C63000(1)
Solde
--
2.0-4.0
0.20
0.30
9.0-11.0
1.5
0.25
4.0-5.5(4)
--
C63010(2)
78.0min
--
2.0-3.5
0.20
0.30
9.7-10.9
1.5
--
4.5-5.5(4)
--
C63020(1)
74.5min
0.03
4.0-5.5
0.25
0.30
10.0-11.0
1.5
--
4.2-6.0(4)
0.05
Cr
0.20
Co
C63200(1)
Solde
0.02
3.5-4.3(5)
--
--
8.7-9.5
1.2-2.0
0.10
4.0-4.8(4)
--
C63280(1)
Solde
0.02
3.0-5.0
--
--
8.5-9.5
0.6-3.5
--
4.0-5.5(4)
--
C63380(1)
Solde
0.02
2.0-4.0
--
0.15
7.0-8.5
11.0-14.0
0.10
1.5-3.0(4)
--
C63400(1)
Solde
0.05
0.15
0.20
0.50
2.6-3.2
--
0.25-0.45
.15(4)
0.15
As
C63600(1)
Solde
0.05
0.15
0.20
0.50
3.0-4.0
--
0.7-1.3
0.15(4)
0.15
As
C63800(1)
Solde
0.05
0.20
--
0.8
2.5-3.1
0.10
1.5-2.1
0.20(6)
0.25-0.55
Co
C64200(1)
Solde
0.05
0.30
0.20
0.50
6.3-7.6
0.10
1.5-2.2
0.25(4)
0.15
As
C64210(1)
Solde
0.05
0.30
0.20
0.50
6.3-7.0
0.10
1.5-2.0
0.25(4)
0.15
As
(1) : Cu + named agents,
99.5% min.
(2) : Cu + named agents,
99.8% min.
(4) : The Ni value includes Co.
(5) : The quantity of Fe must not exceed the quantity of Ni
(6) : Does not include Co.
Top of the page
Wrought bronzes with silicon:
Alloy number
Cu
Pb
Fe
Sn
Zn
Mn
Si
Ni
Other agents
(incl
Ag)
C64700(1)
Solde
0.10
0.10
--
0.50
--
0.40-0.8
1.6-2.2(2)
--
C64710(1)
95.0min
--
--
--
0.20-0.50
0.10
0.500-.9
2.9-3.5(2)
--
C64725(1)
95.0min
0.01
0.25
0.20-0.8
0.50-1.5
--
0.20-0.8
1.3-2.7(2)
0.01
Ca
0.20
Cr
0.20
Mg
C64730(1)
93.5min
--
--
1.0-1.5
0.20-0.50
0.10
0.50-0.9
2.9-3.5(2)
--
C64740(1)
95.0min
0.01
0.25
1.5-2.5
0.20-1.0
--
0.05-0.50
1.0-2.0(2)
0.01
Ca
0.05
Mg
C64750(3)
Solde
--
1.0
0.05-0.8
1.0
--
0.10-0.7
1.0-3.0
0.10
Mg
0.10
P
0.10
Zr
C64760(1)
93.5min
0.02
--
0.30
0.20-2.5
--
0.05-0.6
0.40-2.5
.05
Mg
C64770(1)
Solde
0.05
0.10
0.05-0.50
0.30-0.8
0.10
0.40-0.8
1.5-3.0(2)
0.30
Mg
C64780(1)
90.0min
0.02
--
0.1-2.0
0.20-2.5
0.01-1.0
0.20-1.9
1.0-3.5
0.01
Cr
0.01
Mg
0.01
Ti
0.01
Zr
C64900(1)
Solde
0.05
0.10
1.2-1.6
0.20
--
0.8-1.2
0.10(2)
0.10
Al
C65100(1)
Solde
0.05
0.8
--
1.5
0.7
0.8-2.0
--
--
C65400(1)
Solde
0.05
--
1.2-1.9
0.50
--
2.7-3.4
--
0.01-0.12
Cr
C65500(1)
Solde
0.05
0.8
--
1.5
0.50-1.3
2.8-3.8
0.6(2)
--
C65600(1)
Solde
0.02
0.50
1.5
1.5
1.5
2.8-4.0
--
0.01
Al
C66100(1)
Solde
0.20-0.8
0.25
--
1.5
1.5
2.8-3.5
--
--
(1) : Cu + named agents,
99.5% min.
(2) : The Ni value includes Co.
(3) : Cu + named agents,
99.92% min.
Top of the page
Wrought complex brass:
Alloy number
Cu
Pb
Fe
Sn
Zn
Ni
Al
Mn
Si
Other agents
(incl
Ag)
C66200(1)
86.6-91.0
0.05
0.05
0.20-0.7
Solde
0.30-1.0(2)
--
--
--
0.05-0.20
P
C66300(1)
84.5-87.5
0.05
1.4-2.4(3)
1.5-3.0
Solde
--
--
--
--
0.20
Co(3)
0.35
P
C66400(1)
Solde
0.015
1.3-1.7(4)
0.05
11.0-12.0
--
--
--
--
0.30-0.7
Co(4)
C66410(1)
Solde
0.015
1.8-2.3
0.05
11.0-12.0
--
--
--
--
--
C66420(1)
Solde
--
0.50-1.5
--
12.7-17.0
--
--
--
--
--
C66430(1)
Solde
0.05
0.6-0.9
0.6-0.9
13.0-15.0
--
--
--
--
0.10
P
C66700(1)
68.5-71.5
0.07
0.10
--
Solde
--
--
0.8-1.5
--
--
C66800(1)
60.0-63.0
0.50
0.35
0.30
Solde
0.25(2)
0.25
2.0-3.5
0.50-1.5
--
C66900(5)
62.5-64.5
0.05
0.25
--
Solde
--
--
11.5-12.5
--
--
C66950(1)
Solde
0.01
0.50
--
14.0-15.0
--
1.0-1.5
14.0-15.0
--
--
C67000(1)
63.0-68.0
0.20
2.0-4.0
0.50
Solde
--
3.0-6.0
2.5-5.0
--
--
C67300(1)
58.0-63.0
0.40-3.0
0.50
0.30
Solde
0.25(2)
0.25
2.0-3.5
0.50-1.5
--
C67400(1)
57.0-60.0
0.50
0.35
0.30
Solde
0.25(2)
0.50-2.0
2.0-3.5
0.50-1.5
--
C67420(1)
57.0-58.5
0.25-0.8
0.15-0.55
0.35
Solde
0.25(2)
1.0-2.0
1.5-2.5
0.25-0.7
--
C67500(1)
57.0-60.0
0.20
0.8-2.0
0.50-1.5
Solde
--
0.25
0.05-0.50
--
--
C67600(1)
57.0-60.0
0.50-1.0
0.40-1.3
0.50-1.5
Solde
--
--
0.05-0.50
--
--
C68000(1)
56.0-60.0
0.05
0.25-1.25
0.75-1.10
Solde
0.20-0.8(2)
.01
0.01-0.50
0.04-0.15
--
C68100(1)
56.0-60.0
0.05
0.25-1.2
0.75-1.10
Solde
--
0.01
0.01-0.50
0.04-0.15
--
C68700(1)
76.0-79.0
0.07
0.06
--
Solde
--
1.8-2.5
--
--
0.02-0.06
As
C68800(1)
Solde
0.05
0.20
--
21.3-24.1(6)
--
3.0-3.8(6)
--
--
0.25-0.55
Co
C69050(1)
70.0-75.0
--
--
--
Solde
0.50-1.5(2)
3.0-4.0
--
0.10-0.6
0.01-0.20
Zr
C69100(1)
81.0-84.0
0.05
0.25
0.10
Solde
0.8-1.4(2)
0.7-1.2
0.10
0.8-1.3
--
C69400(1)
80.0-83.0
0.30
0.20
--
Solde
--
--
--
3.5-4.5
--
C69430(1)
80.0-83.0
0.30
0.20
--
Solde
--
--
--
3.5-4.5
0.03-0.06
As
C69700(1)
75.0-80.0
0.50-1.5
0.20
--
Solde
--
--
0.40
2.5-3.5
--
C69710(1)
75.0-80.0
0.50-1.5
0.20
--
Solde
--
--
0.40
2.5-3.5
0.03-0.06
As
C69750(1)
78.0-83.0
0.8-1.3
0.05
0.05
Solde
0.01
--
0.05
1.9-2.22
0.02
P
(1) : Cu + named agents,
99.5% min.
(2) : The Ni value includes Co.
(3) : Fe + Co, 1.4 - 2.4%
(4) : Fe + Co, 1.8 - 2.3%.
(5) : Cu + named agents,
99.8% min.
(6) : Al + Zn, 25.1 - 27.1%.
Top of the page
Wrought cupro-nickel:
Alloy number
Cu
Pb
Fe
Zn
Ni
Sn
Mn
Other agents
(incl
Ag)
C70100(1)
Solde
--
0.05
0.25
3.0-4.0(2)
--
0.50
--
C70200(1)
Solde
0.05
0.10
--
2.0-3.0(2)
--
0.40
--
C70230(1)
Solde
--
--
0.50-2.0
2.2-3.2
0.10-0.50
--
(3)
0.40-0.8
Si
0.10
Ag
C70250(1)
Solde
0.05
0.20
1.0
2.2-4.2(2)
--
0.10
0.05-0.30
Mg
0.25-1.2
Si
C70260(1)
Solde
--
--
--
1.0-3.0(2)
--
--
0.010
P
0.20-0.7
Si
C70270(1)
Solde
0.05
0.28-1.0
1.0
1.0-3.0(2)
0.10-1.0
0.15
0.20-1.0
Si
C70280(1)
Solde
0.02
0.015
0.30
1.3-1.7(2)
1.0-1.5
--
0.02-0.04
P
0.22-0.30
Si
C70290(1)
Solde
0.02
0.015
0.30
1.3-1.7(2)
2.1-2.7
--
0.02-0.04
P
0.22-0.30
Si
C70400(1)
Solde
0.05
1.3-1.7
1.0
4.8-6.2(2)
--
0.30-0.8
--
C70500(1)
Solde
0.05
0.10
0.20
5.8-7.8(2)
--
0.15
--
C70600(1)
Solde
0.05
1.0-1.8
1.0
9.0-11.0(2)
--
1.0
--
C70610(1)
Solde
0.01
1.0-2.0
--
10.0-11.0(2)
--
0.50-1.0
0.05
C
0.05
S
C70620(1)
86.5min
0.02
1.0-1.8
0.50
9.0-11.0(2)
--
1.0
0.05
C
0.02
P
0.02
S
C70690(1)
Solde
0.001
0.005
0.001
9.0-11.0(2)
--
0.001
(4)
C70700(1)
Solde
--
0.05
--
9.5-10.5(2)
--
0.50
--
C70800(1)
Solde
0.05
0.10
0.20
10.5-12.5(2)
--
0.15
--
C71000(1)
Solde
0.05
1.0
1.0
19.0-23.0(2)
--
1.0
--
C71100(1)
Solde
0.05
0.10
0.20
22.0-24.0(2)
--
0.15
--
C71300(1)
Solde
0.05
0.20
1.0
23.5-26.5(2)
--
1.0
--
C71500(1)
Solde
0.05
0.40-1.0
1.0
29.0-33.0(2)
--
1.0
--
C71520(1)
65.0min
0.02
0.40-1.0
0.50
29.0-33.0(2)
--
1.0
0.05
C
0.02
P
0.02
S
C71580(1)
Solde
0.05
0.50
0.05
29.0-33.0(2)
--
0.30
(5)
C71581(1)
Solde
0.02
0.40-0.7
--
29.0-32.0(2)
--
1.0
(6)
C71590
Solde
0.001
0.15
0.001
29.0-31.0(2)
0.001
0.50
(4)
C71640(1)
Solde
0.05(7)
1.7-2.3
1.0(7)
29.0-32.0(2)
--
1.5-2.5
(7)
0.06
C
0.03
S
C71700(1)
Solde
--
0.40-1.0
--
29.0-33.0(2)
--
--
0.30-0.7
Be
C71900(1)
Solde
0.015
0.50
0.05
28.0-33.0(2)
--
0.20-1.0
0.04
C
2.2-3.0
Cr
0.02
P
0.25
Si
0.015
S
0.01-0.20
Ti
0.02-0.35
Zr
C72150(1)
Solde
0.05
0.10
0.20
43.0-46.0(2)
--
0.05
0.10
C
0.50
Si
C72200(8)
Solde
0.05(7)
0.50-1.0
1.0(7)
15.0-18.0(2)
--
1.0
(7)
0.30-0.7
Cr
0.03
Si
0.03
Ti
C72420(9)
Solde
0.02
0.7-1.2
0.20
13.5-16.5(2)
0.10
3.5-5.5
1.0-2.0
Al
0.05
C
0.50
Cr
0.05
Mg
0.01
P
0.15
Si
0.15
S
C72500(8)
Solde
0.05
0.6
0.50
8.5-10.5(2)
1.8-2.8
0.20
--
C72650(9)
Solde
0.01
0.10
0.10
7.0-8.0(2)
4.5-5.5
0.10
--
C72700(9)
Solde
0.02(10)
0.50
0.50
8.5-9.5(2)
5.5-6.5
0.05-0.30
0.15
Mg
0.10
Nb
C72800(9)
Solde
0.005
0.50
1.0
9.5-10.5(2)
7.5-8.5
0.05-0.30
0.10
Al
0.02
Sb
0.001
Bi
0.001
B
0.005-0.15
Mg
0.10-0.30
Nb
0.005
P
0.05
Si
0.0025
S
0.01
Ti
C72900(9)
Solde
0.02(10)
0.50
0.50
14.5-15.5(2)
7.5-8.5
0.30
0.15
Mg
0.10
Nb
C72950(9)
Solde
0.05
0.6
--
20.0-22.0(2)
4.5-5.7
0.6
--
(1) : Cu + named agents,
99.5% min.
(2) : The Ni value includes Co.
(3) : The Ag value includes B
(4) : The maximal limit of additionnal agents is: 0.02% C,0.015%
Si,0.003% S,0.002% Al, 0.001% P,0.0005%Hg,0.001% Ti,0.001% Sb,0.001%
As,0.001% Bi,0.05% Co,0.10% Mg et0.005% Oxygen. Pour C70690, Co peut être
0.02% max.
(5) : The maximal limit of additionnal agents is: 0.07% C, 0.15%
Si, 0.024% S, 0.05% Al et 0.03% P.
(6) : 0.02% P, max.; 0.25% Si, max.; 0.01% S, max.; 0.02 - 0.50%
Ti.
8) : Cu + named agents,
99.8% min.
(9) : Cu + named agents,
99.7% min.
(10) :0.005% Pb, max. for hot rolling
Top of the page
Alloy number
Cu
Pb
Fe
Zn
Ni
Mn
Other agents
(incl
Ag)
C73500(1)
70.5-73.5
0.10
0.25
Solde
16.5-19.5(2)
0.50
--
C74000(1)
69.0-73.5
0.10
0.25
Solde
9.0-11.0(2)
0.50
--
C74300(1)
63.0-66.0
0.10
0.25
Solde
7.0-9.0(2)
0.50
--
C74400(3)
62.0-66.0
0.05
0.05
Solde
2.0-4.0(2)
--
--
C74500(1)
63.5-66.5
0.10(4)
0.25
Solde
9.0-11.0(2)
0.50
--
C75200(1)
63.0-66.5
0.05
0.25
Solde
16.5-19.5(2)
0.50
--
C75400(1)
63.5-66.5
0.10
0.25
Solde
14.0-16.0(2)
0.50
--
C75700(1)
63.5-66.5
0.05
0.25
Solde
11.0-13.0(2)
0.50
--
C76000(1)
60.0-63.0
0.10
0.25
Solde
7.0-9.0(2)
0.50
--
C76200(1)
57.0-61.0
0.10
0.25
Solde
11.0-13.5(2)
0.50
--
C76400(1)
58.5-61.5
0.05
0.25
Solde
16.5-19.5(2)
0.50
--
C76700(1)
55.0-58.0
--
--
Solde
14.0-16.0(2)
0.50
--
C77000(1)
53.5-56.5
0.05
0.25
Solde
16.5-19.5(2)
0.50
--
C77300(1)
46.0-50.0
0.05
--
Solde
9.0-11.0(2)
--
0.01
Al
0.25
P
0.04-0.25
Si
C77400(1)
43.0-47.0
0.20
--
Solde
9.0-11.0(2)
--
--
C77600(1)
42.0-45.0
0.25
0.20
Solde
12.0-14.0(2)
0.25
0.15
Sn
C78200(1)
63.0-67.0
1.5-2.5
0.35
Solde
7.0-9.0(2)
0.50
--
C79000(1)
63.0-67.0
1.5-2.2
0.35
Solde
11.0-13.0(2)
0.50
--
C79200(1)
59.0-66.5
0.8-1.4
0.25
Solde
11.0-13.0(2)
0.50
--
C79350(1)
59.0-63.0
0.8-1.1
0.25
Solde
23.0-26.0(2)
0.50
0.40-0.6
Sn
C79800(1)
45.5-48.5
1.5-2.5
0.25
Solde
9.0-11.0(2)
1.5-2.5
--
C79830(1)
45.5-47.0
1.0-2.5
0.45
Solde
9.0-10.5(2)
0.15-0.55
--
C79860(5)
42.3-43.7
1.3-1.8
0.20
Solde
11.8-12.7(2)
5.6-6.4
0.005
P
0.06
Si
0.10
Sn
(1) : Cu + named agents,
99.5% min.
(2) : The Ni value includes Co.
(3) : Cu + named agents,
99.7% min.
(4) : 0.05% Pb, max.pour ronds, fils et tubes
(5) : Cu + named agents,
99.8% min.
Top of the page
Cast pure coppers:
Alloy number
Cu
P
Other agents
(incl
Ag)
C80100
99.95min
--
--
C80410
99.9min
--
--
C81100
99.70min
--
--
C81200
99.9min
0.045-0.065
--
Top of the page
Cast lowly alloyed coppers:
Alloy number
Cu
Be
Co
Si
Ni
Fe
Al
Sn
Pb
Zn
Cr
C81400(1)
Solde
0.02-0.10
--
--
--
--
--
--
--
--
0.6-1.0
C81500(1)
Solde
--
--
0.15
--
0.10
0.10
0.10
0.02
0.10
0.40-1.5
C81540(1)
95.1min(2)
--
--
0.40-0.8
2.0-3.0(3)
0.15
0.10
0.10
0.02
0.10
0.10-0.6
C82000(1)
Solde
0.45-0.8
2.40-2.70(4)
0.15
0.20(4)
0.10
0.10
0.10
0.02
0.10
0.10
C82200(1)
Solde
0.35-0.8
0.30
--
1.0-2.0
--
--
--
--
--
--
C82400(1)
Solde
1.60-1.85
0.20-0.65
--
0.20
0.20
0.15
0.10
0.02
0.10
0.10
C82500(1)
Solde
1.90-2.25
0.35-0.70(4)
0.20-0.35
0.20(4)
0.25
0.15
0.10
0.02
0.10
0.10
C82510(1)
Solde
1.90-2.15
1.0-1.2
0.20-0.35
0.20
0.25
0.15
0.10
0.02
0.10
0.10
C82600(1)
Solde
2.25-2.55
0.35-0.65
0.20-0.35
0.20
0.25
0.15
0.10
0.02
0.10
0.10
C82700(1)
Solde
2.35-2.55
--
0.15
1.0-1.5
0.25
0.15
0.10
0.02
0.10
0.10
C82800(1)
Solde
2.50-2.85
0.35-0.70(4)
0.20-0.35
0.20(4)
0.25
0.15
0.10
0.02
0.10
0.10
(1) : Cu + named agents,
99.5% min.
(2) : Includes Ag.
(3) : The Ni value includes Co.
(4) : Ni + Co.
Top of the page
Cast brass:
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
As
Ni
S
P
Al
Si
C83300(1)
92.0-94.0(2)
1.0-2.0
1.0-2.0
2.0-6.0
--
--
--
--
--
--
--
--
C83400(1)
88.0-92.0(2)
0.20
0.50
8.0-12.0
0.25
0.25
--
1.0(3)
0.08
0.03(4)
0.005
0.005
C83450(1)
87.0-89.0(2)
2.0-3.5
1.5-3.0
5.5-7.5
0.30
0.25
--
0.8-2.0(3)
0.08
0.03(4)
0.005
0.005
C83500(1)
86.0-88.0(2)
5.5-6.5
3.5-5.5
1.0-2.5
0.25
0.25
--
0.50-1.0(3)
0.08
0.03(4)
0.005
0.005
C83600(1)
84.0-86.0(2)
4.0-6.0
4.0-6.0
4.0-6.0
0.30
0.25
--
1.0(3)
0.08
0.05(4)
0.005
0.005
C83800(1)
82.0-83.8(2)
3.3-4.2
5.0-7.0
5.0-8.0
0.30
0.25
--
1.0(3)
0.08
0.03(4)
0.005
0.005
C83810(1)
Solde(2)
2.0-3.5
4.0-6.0
7.5-9.5
0.50(5)
--
--
2.0(3)
--
--
0.005
0.10
(1) : Cu + named agents,
99.3% min
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
(4) : In continuous casting,
P is 1.5%, max.
(5) : Fe + Sb + As is 0.50% max.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
S
P
Al
Si
Bi
Other agents
C84200(1)
78.0-82.0(2)
4.0-6.0
2.0-3.0
10.0-16.0
0.40
0.25
0.8(3)
0.08
0.05(4)
0.005
0.005
--
--
C84400(1)
78.0-82.0(2)
2.3-3.5
6.0-8.0
7.0-10.0
0.40
0.25
1.0(3)
0.08
0.02(4)
0.005
0.005
--
--
C84410(1)
Solde(2)
3.0-4.5
7.0-9.0
7.0-11.0
--
--
1.0(3)
--
--
0.01
0.2
0.05
(5)
C84500(1)
77.0-79.0(2)
2.0-4.0
6.0-7.5
10.0-14.0
0.40
0.25
1.0(3)
0.08
0.02(4)
0.005
0.005
--
--
C84800(1)
75.0-77.0(2)
2.0-3.0
5.5-7.0
13.0-17.0
0.40
0.25
1.0(3)
0.08
0.02(4)
0.005
0.005
--
--
(1) : Cu + named agents,
99.3% min.
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
(4) : In continuous casting,
P is 1.5%, max.
(5) : Fe + Sb + As is 0.80% max.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
Mn
As
S
P
Al
Si
C85200(1)
70.0-74.0(2)
0.7-2.0
1.5-3.8
20.0-27.0
0.6
0.20
1.0(3)
--
--
0.05
0.02
0.005
0.05
C85400(4)
65.0-70.0(2)
0.50-1.5
1.5-3.8
24.0-32.0
0.7
--
1.0(3)
--
--
--
--
0.35
0.05
C85500(1)
59.0-63.0(2)
0.20
0.20
Solde
0.20
--
0.20(3)
0.20
--
--
--
--
--
C85700(5)
58.0-64.0(2)
0.50-1.5
0.8-1.5
32.0-40.0
0.7
--
1.0(3)
--
--
--
--
0.8
0.05
C85800(5)
57.0min(2)
1.5
1.5
31.0-41.0
0.50
0.05
0.50(3)
0.25
0.05
0.05
0.01
0.55
0.25
(1) : Cu + named agents,
99.1% min.
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
(4) : Cu + named agents,
98.9% min.
(5) : Cu + named agents,
98.7% min.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Ni
Al
Mn
Si
C86100(1)
66.0-68.0(2)
0.20
0.20
Solde
2.0-4.0
--
4.5-5.5
2.5-5.0
--
C86200(1)
60.0-66.0(2)
0.20
0.20
22.0-28.0
2.0-4.0
1.0(3)
3.0-4.9
2.5-5.0
--
C86300(1)
60.0-66.0(2)
0.20
0.20
22.0-28.0
2.0-4.0
1.0(3)
5.0-7.5
2.5-5.0
--
C86400(1)
56.0-62.0(2)
0.50-1.5
0.50-1.5
34.0-42.0
0.40-2.0
1.0(3)
0.50-1.5
0.10-1.5
--
C86500(1)
55.0-60.0(2)
1.0
0.40
36.0-42.0
0.40-2.0
1.0(3)
0.50-1.5
0.10-1.5
--
C86550(1)
57.0min(2)
1.0
0.50
Solde
0.7-2.0
1.0(3)
0.50-2.5
0.10-3.0
0.10
C86700(1)
55.0-60.0(2)
1.5
0.50-1.5
30.0-38.0
1.0-3.0
1.0(3)
1.0-3.0
0.10-3.5
--
C86800(1)
53.5-57.0(2)
1.0
0.20
Solde
1.0-2.5
2.5-4.0(3)
2.0
2.5-4.0
--
(1) : Cu + named agents,
99.0% min.
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
Top of the page
Cast bronzes with silicon:
Alloy number
Cu
Sn
Pb
Zn
Fe
Al
Si
Mn
Mg
Ni
S
Other agents
C87300(1)
94.0min
--
0.20
0.25
0.20
--
3.5-4.5
0.8-1.5
--
--
--
--
C87400(2)
79.0min
--
1.0
12.0-16.0
--
0.8
2.5-4.0
--
--
--
--
--
C87500(1)
79.0min
--
0.50
12.0-16.0
--
0.50
3.0-5.0
--
--
--
--
--
C87600(1)
88.0min
--
0.50
4.0-7.0
0.20
--
3.5-5.5
0.25
--
--
--
--
C87610(1)
90.0min
--
0.20
3.0-5.0
0.20
--
3.0-5.0
0.25
--
--
--
--
C87800(1)
80.0min
0.25
0.15
12.0-16.0
0.15
0.15
3.8-4.2
0.15
0.01
0.20(3)
0.05
0.05
Sb
0.05
As
0.01
P
(1) : Cu + named agents,
99.5% min.
(2) : Cu + named agents,
99.2% min.
(3) : The Ni value includes Co.
Top of the page
Cast special bronzes:
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
S
P
Al
Si
Bi
Se
Autres
Eléments
C89320(1)
87.0-91.0
5.0-7.0
0.09
1.0
0.20
0.35
1.0(2)
0.08
0.30
0.005
0.005
4.0-6.0
--
--
C89325(3)
84.0-88.0
9.0-11.0
0.10
1.0
0.15
0.50
1.0(2)
0.08
0.10
0.005
0.005
2.7-3.7
--
(4)
C89510(1)
86.0-88.0
4.0-6.0
0.25
4.0-6.0
0.20
0.25
1.0(2)
0.08
0.05
0.005
0.005
0.50-1.5(5)
0.35-0.75(5)
--
C89520(1)
85.0-87.0
5.0-6.0
0.25
4.0-6.0
0.20
0.25
1.0(2)
0.08
0.05
0.005
0.005
1.6-2.2(6)
0.8-1.1(6)
--
C89550(1)
58.0-64.0
1.2
0.10
32.0-38.0
0.50
0.05
1.0(2)
0.05
0.01
0.10-0.6
0.25
0.6-1.2
0.01-0.10
--
C89831(3)
87.0-91.0
2.7-3.7
0.10
2.0-4.0
0.30
0.25
1.0(2)
0.08
0.05
0.005
0.005
2.7-3.7
--
(4)
C89833(3)
87.0-91.0
4.0-6.0
0.10
2.0-4.0
0.30
0.25
1.0(2)
0.08
0.05
0.005
0.005
1.7-2.7
--
(4)
C89835(3)
85.0-89.0
6.0-7.5
0.10
2.0-4.0
0.20
0.35
1.0(2)
0.08
0.10
0.005
0.005
1.7-2.7
--
(4)
C89837(3)
84.0-88.0
3.0-4.0
0.10
6.0-10.0
0.30
0.25
1.0(2)
0.08
0.05
0.005
0.005
0.7-1.2
--
(4)
C89844(7)
83.0-86.0
3.0-5.0
0.20
7.0-10.0
0.30
0.25
1.0(2)
0.08
0.05
0.005
0.005
2.0-4.0
--
--
C89940(1)
64.0-68.0
3.0-5.0
0.01
3.0-5.0
0.7-2.0
0.10
20.0-23.0(2)
0.05
0.10-0.15
0.005
0.15
4.0-5.5
--
0.20
Mn
(1) : Cu + named agents,
99.5% min.
(2) : The Ni value includes Co.
(3) : Cu + named agents,
99.0% min.
(5) : Bi:Se >= 2:1
(6) : Bi:Se >= 2:1
(7) : Cu + named agents,
99.3% min.
Top of the page
Cast bronzes
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
S
P
Al
Si
C90200(1)
91.0-94.0(2)
6.0-8.0
0.30
0.50
0.20
0.20
0.50(3)
0.05
0.05(4)
0.005
0.005
C90300(1)
86.0-89.0(2)
7.5-9.0
0.30
3.0-5.0
0.20
0.20
1.0(3)
0.05
0.05(4)
0.005
0.005
C90500(5)
86.0-89.0(2)
9.0-11.0
0.30
1.0-3.0
0.20
0.20
1.0(3)
0.05
0.05(4)
0.005
0.005
C90700(1)
88.0-90.0(2)
10.0-12.0
0.50
0.50
0.15
0.20
0.50(3)
0.05
0.30(4)
0.005
0.005
C90710(1)
Solde(2)
10.0-12.0
0.25
0.05
0.10
0.20
0.10(3)
0.05
0.05-1.2(4)
0.005
0.005
C90800(1)
85.0-89.0(2)
11.0-13.0
0.25
0.25
0.15
0.20
0.50(3)
0.05
0.30(4)
0.005
0.005
C90810(1)
Solde(2)
11.0-13.0
0.25
0.30
0.15
0.20
0.50(3)
0.05
0.15-0.8(4)
0.005
0.005
C90900(1)
86.0-89.0(2)
12.0-14.0
0.25
0.25
0.15
0.20
0.50(3)
0.05
0.05(4)
0.005
0.005
C91000(1)
84.0-86.0(2)
14.0-16.0
0.20
1.5
0.10
0.20
0.8(3)
0.05
0.05(4)
0.005
0.005
C91100(1)
82.0-85.0(2)
15.0-17.0
0.25
0.25
0.25
0.20
0.50(3)
0.05
1.0(4)
0.005
0.005
C91300(1)
79.0-82.0(2)
18.0-20.0
0.25
0.25
0.25
0.20
0.50(3)
0.05
1.0(4)
0.005
0.005
C91600(1)
86.0-89.0(2)
9.7-10.8
0.25
0.25
0.20
0.20
1.2-2.0(3)
0.05
0.30(4)
0.005
0.005
C91700(1)
84.0-87.0(2)
11.3-12.5
0.25
0.25
0.20
0.20
1.2-2.0(3)
0.05
0.30(4)
0.005
0.005
(1) : Cu + named agents,
99.4% min..
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
(4) : In continuous casting,
P is 1.5%, max.
(5) : Cu + named agents,
99.7% min.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
S
P
Al
Si
Mn
C92200(1)
86.0-90.0(2)
5.5-6.5
1.0-2.0
3.0-5.0
0.25
0.25
1.0(3)
0.05
0.05(4)
0.005
0.005
--
C92210(1)
86.0-89.0(2)
4.5-5.5
1.7-2.5
3.0-4.5
0.25
0.20
0.7-1.0(3)
0.05
0.03(4)
0.005
0.005
--
C92220(1)
86.0-88.0(2)
5.0-6.0
1.5-2.5
3.0-5.5
0.25
--
0.50-1.0(3)
--
0.05(4)
--
--
--
C92300(1)
85.0-89.0(2)
7.5-9.0
.30-1.0
2.5-5.0
0.25
0.25
1.0(3)
0.05
0.05(4)
0.005
0.005
--
C92310(1)
Solde(2)
7.5-8.5
.30-1.5
3.5-4.5
--
--
1.0(3)
--
--
0.005
0.005
0.03
C92400(1)
86.0-89.0(2)
9.0-11.0
1.0-2.5
1.0-3.0
0.25
0.25
1.0(3)
0.05
0.05(4)
0.005
0.005
--
C92410(1)
Solde(2)
6.0-8.0
2.5-3.5
1.5-3.0
0.20
0.25
0.20(3)
--
--
0.005
0.005
0.05
C92500(1)
85.0-88.0(2)
10.0-12.0
1.0-1.5
0.50
0.30
0.25
0.8-1.5(3)
0.05
0.30(4)
0.005
0.005
--
C92600(1)
86.0-88.5(2)
9.3-10.5
0.8-1.5
1.3-2.5
0.20
0.25
0.7(3)
0.05
0.03(4)
0.005
0.005
--
C92610(1)
Solde(2)
9.5-10.5
0.30-1.5
1.7-2.8
0.15
--
1.0(3)
--
--
0.005
0.005
0.03
C92700(1)
86.0-89.0(2)
9.0-11.0
1.0-2.5
0.7
0.20
0.25
1.0(3)
0.05
0.25(4)
0.005
0.005
--
C92710(1)
Solde(2)
9.0-11.0
4.0-6.0
1.0
0.20
0.25
2.0(3)
0.05
0.10(4)
0.005
0.005
--
C92800(1)
78.0-82.0(2)
15.0-17.0
4.0-6.0
0.8
0.20
0.25
0.8(3)
0.05
0.05(4)
0.005
0.005
--
C92810(1)
78.0-82.0(2)
12.0-14.0
4.0-6.0
0.50
0.50
0.25
0.8-1.2(3)
0.05
0.05(4)
0.005
0.005
--
C92900(1)
82.0-86.0(2)
9.0-11.0
2.0-3.2
0.25
0.20
0.25
2.8-4.0(3)
0.05
0.50(4)
0.005
0.005
--
(1) : Cu + named agents,
99.3% min.
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
(4) : In continuous casting,
P is 1.5%, max.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
S
P
Al
Si
C93100(1)
Solde(2)
6.5-8.5
2.0-5.0
2.0
0.25
0.25
1.0(3)
0.05
0.30(4)
0.005
0.005
C93200(1)
81.0-85.0(2)
6.3-7.5
6.0-8.0
1.0-4.0
0.20
0.35
1.0(3)
0.08
0.15(4)
0.005
0.005
C93400(1)
82.0-85.0(2)
7.0-9.0
7.0-9.0
0.8
0.20
0.50
1.0(3)
0.08
0.50(4)
0.005
0.005
C93500(1)
83.0-86.0(2)
4.3-6.0
8.0-10.0
2.0
0.20
0.30
1.0(3)
0.08
0.05(4)
0.005
0.005
C93600(5)
79.0-83.0
6.0-8.0
11.0-13.0
1.0
0.20
0.55
1.0(3)
0.08
0.15(4)
0.005
0.005
C93700(1)
78.0-82.0
9.0-11.0
8.0-11.0
0.8
0.7(6)
0.50
0.50(3)
0.08
0.10(4)
0.005
0.005
C93720(1)
83.0min
3.5-4.5
7.0-9.0
4.0
0.7
0.50
0.50(3)
--
0.10(4)
--
--
C93800(1)
75.0-79.0
6.3-7.5
13.0-16.0
0.8
0.15
0.8
1.0(3)
0.08
0.05(4)
0.005
0.005
C93900(7)
76.5-79.5
5.0-7.0
14.0-18.0
1.5
0.40
0.50
0.8(3)
0.08
1.5(4)
0.005
0.005
C94000(8)
69.0-72.0
12.0-14.0
14.0-16.0
0.50
0.25
0.50
0.50-1.0(3)
0.08(9)
0.05(4)
0.005
0.005
C94100(8)
72.0-79.0
4.5-6.5
18.0-22.0
1.0
0.25
0.8
1.0(3)
0.08(9)
0.50(4)
0.005
0.005
C94300(1)
67.0-72.0
4.5-6.0
23.0-27.0
0.8
0.15
0.8
1.0(3)
0.08(9)
0.08(4)
0.005
0.005
C94310(1)
Solde
1.5-3.0
27.0-34.0
0.50
0.50
0.50
0.25-1.0(3)
--
0.05(4)
--
--
C94320(1)
Solde
4.0-7.0
24.0-32.0
--
0.35
--
--
--
--
--
--
C94330(1)
68.5-75.5
3.0-4.0
21.0-25.0
3.0
0.7
0.50
0.50(3)
--
0.10(4)
--
--
C94400(1)
Solde
7.0-9.0
9.0-12.0
0.8
0.15
0.8
1.0(3)
0.08
0.50(4)
0.005
0.005
C94500(1)
Solde
6.0-8.0
16.0-22.0
1.2
0.15
0.8
1.0(3)
0.08
0.05(4)
0.005
0.005
(1) : Cu + named agents,
99.0% min.
(2) : To determine Cu min., Cu must be calculated by
Cu + Ni.
(3) : The Ni value includes Co.
(4) : In continuous casting,
P est de 1.5%, max.
(5) : Cu + named agents,
99.3% min.
(6) : Fe is 0.35% max.
(7) : Cu + named agents,
98.9% min.
(8) : Cu + named agents,
98.7% min.
(9) : In continuous casting,
S is 0.25% max.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
Mn
S
P
Al
Si
C94700(1)
85.0-90.0
4.5-6.0
0.10(2)
1.0-2.5
0.25
0.15
4.5-6.0(3)
0.20
0.05
0.05
0.005
0.005
C94800(1)
84.0-89.0
4.5-6.0
0.30-1.0
1.0-2.5
0.25
0.15
4.5-6.0(3)
0.20
0.05
0.05
0.005
0.005
C94900(4)
79.0-81.0
4.0-6.0
4.0-6.0
4.0-6.0
0.30
0.25
4.0-6.0(3)
0.10
0.08
0.05
0.005
0.005
(1) : Cu + named agents,
98.7% min.
(3) : The Ni value includes Co.
(4) : Cu + named agents,
99.4% min.
Top of the page
Cast cupro-aluminium:
Alloy number
Cu
Pb
Fe
Ni
Al
Mn
Mg
Si
Zn
Sn
Other agents
C95200(1)
86.0min
--
2.5-4.0
--
8.5-9.5
--
--
--
--
--
--
C95210(1)
86.0min
0.05
2.5-4.0
1.0(2)
8.5-9.5
1.0
0.05
0.25
0.50
0.10
--
C95220(3)
Solde
--
2.5-4.0
2.5(2)
9.5-10.5
0.50
--
--
--
--
--
C95300(1)
86.0min
--
.8-1.5
--
9.0-11.0
--
--
--
--
--
--
C95400(3)
83.0min
--
3.0-5.0
1.5(2)
10.0-11.5
0.50
--
--
--
--
--
C95410(3)
83.0min
--
3.0-5.0
1.5-2.5(2)
10.0-11.5
0.50
--
--
--
--
--
C95420(3)
83.5min
--
3.0-4.3
.50(2)
10.5-12.0
0.50
--
--
--
--
--
C95500(3)
78.0min
--
3.0-5.0
3.0-5.5(2)
10.0-11.5
3.5
--
--
--
--
--
C95510(4)
78.0min
--
2.0-3.5
4.5-5.5(2)
9.7-10.9
1.5
--
--
0.30
0.20
--
C95520(3)
74.5min
0.03
4.0-5.5
4.2-6.0(2)
10.5-11.5
1.5
--
0.15
0.30
0.25
0.05
Cr
0.20
Co
C95600(1)
88.0min
--
--
0.25(2)
6.0-8.0
--
--
1.8-3.2
--
--
--
C95700(3)
71.0min
--
2.0-4.0
1.5-3.0(2)
7.0-8.5
11.0-14.0
--
0.10
--
--
--
C95710(3)
71.0min
0.05
2.0-4.0
1.5-3.0(2)
7.0-8.5
11.0-14.0
--
0.15
0.50
1.0
0.05
P
C95720(3)
73.0min
0.03
1.5-3.5
3.0-6.0(2)
6.0-8.0
12.0-15.0
--
0.10
0.10
0.10
0.20
Cr
C95800(3)
79.0min
0.03
3.5-4.5(5)
4.0-5.0(5)
8.5-9.5
0.8-1.5
--
0.10
--
--
--
C95810(3)
79.0min
0.10
3.5-4.5(5)
4.0-5.0(5)
8.5-9.5
0.8-1.5
0.05
0.10
0.50
--
--
C95820(6)
77.5min
0.02
4.0-5.0
4.5-5.8(2)
9.0-10.0
1.5
--
0.10
0.20
0.20
--
C95900(3)
Solde
--
3.0-5.0
0.50(2)
12.0-13.5
1.5
--
--
--
--
--
(1) : Cu + named agents,
99.0% min.
(2) : The Ni value includes Co.
(3) : Cu + named agents,
99.5% min.
(4) : Cu + named agents,
99.8% min.
(5) : The Fe quantity must not exceed the quantity of Ni.
(6) : Cu + named agents,
99.2% min.
Top of the page
Cast cupro-nickels:
Alloy number
Cu
Pb
Fe
Ni
Mn
Si
Nb
C
Be
Autres
Eléments
C96200(1)
Solde
0.01
1.0-1.8
9.0-11.0(2)
1.5
0.50
1.0(3)
0.10
--
0.02
P
0.02
S
C96300(1)
Solde
0.01
0.50-1.5
18.0-22.0(2)
0.25-1.5
0.50
0.50-1.5
0.15
--
0.02
P
0.02
S
C96400(1)
Solde
0.01
0.25-1.5
28.0-32.0(2)
1.5
0.50
0.50-1.5
0.15
--
0.02
P
0.02
S
C96600(1)
Solde
0.01
0.8-1.1
29.0-33.0(2)
1.0
0.15
--
--
0.40-0.7
--
C96700(1)
Solde
0.01
0.40-1.0
29.0-33.0(2)
0.40-1.0
0.15
--
--
1.1-1.2
0.15-0.35
Ti
0.15-0.35
Zr
C96800(1) (4)
Solde
0.005
0.50
9.5-10.5(2)
0.05-0.30
0.05
0.10-0.30
--
--
0.005-0.15
Mg
7.5-8.5
Sn
1.0
Zn
C96900(1)
Solde
0.02
0.50
14.5-15.5(2)
0.050-.30
--
0.10
--
--
0.15
Mg
7.5-8.5
Sn
0.50
Zn
C96950(1)
Solde
0.02
0.05
11.0-15.5(2)
0.05-0.40
0.30
0.10
--
--
0.15
Mg
5.8-8.5
Sn
(1) : Cu + named agents,
99.5% min.
(2) : The Ni value includes Co.
(4) : The maximale limit of impurities content is:
10% Al, 0.001%
B, 0.001% Bi, 0.005% P, 0.0025% S, 0.02% Sb, 0.01%Ti.
Top of the page
Alloy number
Cu
Sn
Pb
Zn
Fe
Sb
Ni
S
P
Al
Mn
Si
C97300(1)
53.0-58.0
1.5-3.0
8.0-11.0
17.0-25.0
1.5
0.35
11.0-14.0(2)
0.08
0.05
0.005
0.50
0.15
C97400(1)
58.0-61.0
2.5-3.5
4.5-5.5
Solde
1.5
--
15.5-17.0(2)
--
--
--
0.50
--
C97600(3)
63.0-67.0
3.5-4.5
3.0-5.0
3.0-9.0
1.5
0.25
19.0-21.5(2)
0.08
0.05
0.005
1.0
0.15
C97800(4)
64.0-67.0
4.0-5.5
1.0-2.5
1.0-4.0
1.5
0.20
24.0-27.0(2)
0.08
0.05
0.005
1.0
0.15
(1) : Cu + named agents,
99.0% min.
(2) : The Ni value includes Co.
(3) : Cu + named agents,
99.7% min.
(4) : Cu + named agents,
99.6% min.
Top of the page
Cupro-plomb :
Alloy number
Cu
Sn
Pb
Ag
Zn
P
Fe
Ni
Sb
C98200(1)
Solde
0.6-2.0
21.0-27.0
--
0.50
0.10
0.7
0.50
0.50
C98400(1)
Solde
0.50
26.0-33.0
1.5
0.50
0.10
0.7
0.50
0.50
C98600
60.0-70.0
0.50
30.0-40.0
1.5
--
--
0.35
--
--
C98800
56.5-62.5(2)
0.25
37.5-42.5(3)
5.5(3)
0.10
0.02
0.35
--
--
C98820
Solde
1.0-5.0
40.0-44.0
--
--
--
0.35
--
--
C98840
Solde
1.0-5.0
44.0-58.0
--
--
--
0.35
--
--
(1) : Cu + named agents,
99.5% min.
(2) : Includes Ag
(3) : Pb and Ag can be adjusted for modifying the alloy hardness.
Top of the page
Alliages spéciaux coulés:
Alloy number
Cu
Sn
Pb
Ni
Fe
Al
Co
Si
Mn
Autres
Eléments
C99300(1)
Solde
0.05
0.02
13.5-16.5
0.40-1.0
10.7-11.5
1.0-2.0
0.02
--
--
C99350(1)
Solde
--
0.15
14.5-16.0(2)
1.0
9.5-10.5
--
--
0.25
7.5-9.5
Zn
C99400(1)
Solde
--
0.25
1.0-3.5
1.0-3.0
.50-2.0
--
0.50-2.0
0.50
0.50-5.0
Zn
C99500(1)
Solde
--
0.25
3.5-5.50
3.0-5.0
.50-2.0
--
0.50-2.0
0.50
0.50-2.0
Zn
C99600(1)
Solde
0.10
0.02
0.20
0.20
1.0-2.8
0.20
0.10
39.0-45.0
0.05
C
0.20
Zn
C99700(1)
54.0min
1.0
2.0
4.0-6.0
1.0
0.50-3.0
--
--
11.0-15.0
19.0-25.0
Zn
C99750(1)
55.0-61.0
--
0.50-2.5
5.0
1.0
0.25-3.0
--
--
17.0-23.0
17.0-23.0
Zn
(1) : Cu + named agents,
99.7% min.
(2) : The Ni value includes Co.
Top of the page