CuNi1P (CW108C)

 

Good resistance, ductility and conductivity.
Chemical compound %
Agent
Cu
Al
Fe
Mn
Ni
P
Si
Sn
Zn
Other
Mass-volume g/cm3
Mini:

Reste

-

-

-

0,8

0,15

-

-

-

-

8,9

 

Maxi:

-

-

-

-

1,2

0,25

-

-

-

0,1

 

Mechanical properties of bars for general usings (EN 12163) :

State
Implementation
Diameter or size/flats mm
Tensile strength Rm N/mm˛ min.
Conventional elastic limit at 0,2 Rp0,2 N/mm²
Stretching
Hardness
from
more than
until
A100mm % min.
A11,3 % min.
A % min.
HB min.
HB max.
HV min.
HV max.

M

 

2

-

80

-

-

-

-

-

-

 -

-

-

 R2502

 

 2

 -

 80

 250

 (140)

 25

 22

25

 -

 -

 -

 -

H0652

 

2

-

80

-

-

-

-

-

65

95

70

100

R5003

 

2

-

25

500

(430)

5

6

8

-

-

-

-

H1353

 

2

-

25

-

-

-

-

-

135

175

140

180

R4503

 

-

25

40

450

(380)

-

-

10

-

-

-

-

H1253

 

-

25

40

-

-

-

-

-

125

175

130

180

R4003

 

-

40

80

400

(330)

-

-

10

-

-

-

-

H1103

 

-

40

80

-

-

-

-

-

110

160

115

165

R6504

 

2

-

80

650

(500)

8

10

12

-

-

-

-

H1904

 

2

-

80

-

-

-

-

-

190

-

200

-

R8005

 

2

-

25

800

(730)

(3)

(4)

5

-

-

-

-

H2205

 

2

-

25

-

-

-

-

-

220

-

230

-

R7505

 

-

25

40

750

(680)

-

-

5

-

-

-

-

H2105

 

-

25

40

-

-

-

-

-

210

-

220

-

R7005

 

-

40

80

700

(630)

-

-

5

-

-

-

-

H2005

 

-

40

80

-

-

-

-

-

200

-

210

-

2 Treated for solution treatment

3 Treated for solution treatment and cold working

4 Treated for solution treatment and age hardening

5 Treated for solution treatment, cold working and age hardening

 

Mechanical properties of wires (EN 12166):

State
Diameter
Tensile strength Rm N/mm˛
Conventional elastic limit at 0,2Rp0,2 N/mm²
Stretching
Hardness HV
from
more than
until
min.
Max.
A100mm % min.
A11,3 % min.
A % min.
min.
max.

M

All sizes

-

-

-

-

-

-

-

-

R250

0,1

-

20,0

250

350

(200)

(3)

7

12

-

-

H090

0,1

-

20,0

-

-

-

-

-

-

90

120

R300

0,1

-

20,0

300

400

(250)

(1)

(3)

8

-

-

H100

0,1

-

20,0

-

-

-

-

-

-

100

130

R360

0,1

-

6,0

360

-

(320)

-

-

-

-

-

H110

0,1

-

6,0

-

-

-

-

-

-

110

-