Moderate conductivity, good erosion resistance.
|
Chemical compound % |
Agent |
Cu |
Be |
Co |
Cr |
Fe |
Mn |
Ni |
Pb |
Si |
Zr |
Other |
Mass-volume g/cm3 |
Mini: |
Reste
|
-
|
-
|
-
|
-
|
-
|
1,0
|
-
|
0,4
|
-
|
-
|
8,8
|
Maxi: |
-
|
-
|
-
|
-
|
0,2
|
0,1
|
1,6
|
0,02
|
0,7
|
-
|
0,3
|
|
|
Mechanical properties of bars for general usings (EN 12163) : |
State |
Implementation |
Diameter or size/flats mm |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2 Rp0,2 N/mm² |
Stretching |
Hardness |
from |
more than |
until |
A100mm
% min. |
A11,3
% min. |
A
% min. |
HB
min. |
HB
max. |
HV
min. |
HV
max. |
M
|
|
2
|
-
|
80
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
R2402
|
|
2
|
-
|
80
|
240
|
(90)
|
25-
|
30
|
35
|
-
|
-
|
-
|
-
|
H0502 |
|
2 |
- |
80 |
- |
- |
- |
- |
- |
50 |
75 |
55 |
80 |
R4103 |
|
2 |
- |
30 |
410 |
(320) |
5 |
7 |
9 |
- |
- |
- |
- |
H1053 |
|
2 |
- |
30 |
- |
- |
- |
- |
- |
105 |
150 |
110 |
155 |
R3503 |
|
- |
30 |
50 |
350 |
(280) |
- |
- |
12 |
- |
- |
- |
- |
H953 |
|
- |
30 |
50 |
- |
- |
- |
- |
- |
95 |
140 |
100 |
145 |
R3003 |
|
- |
50 |
80 |
300 |
(210) |
- |
- |
16 |
- |
- |
- |
- |
H0853 |
|
- |
50 |
80 |
- |
- |
- |
- |
- |
85 |
130 |
90 |
135 |
R4404 |
|
2 |
- |
80 |
440 |
(320) |
12 |
15 |
17 |
- |
- |
- |
- |
H1204 |
|
2 |
- |
80 |
- |
- |
- |
- |
- |
120 |
170 |
125 |
175 |
R5905 |
|
2 |
- |
30 |
590 |
(570) |
8 |
10 |
12 |
- |
- |
- |
- |
H1605 |
|
2 |
- |
30 |
- |
- |
- |
- |
- |
160 |
- |
170 |
- |
R5405 |
|
- |
30 |
50 |
540 |
(450) |
- |
- |
10 |
- |
- |
- |
- |
H1405 |
|
- |
30 |
50 |
- |
- |
- |
- |
- |
140 |
- |
145 |
- |
R5005 |
|
- |
50 |
80 |
500 |
(420) |
- |
- |
10 |
- |
- |
- |
- |
H1255 |
|
- |
50 |
80 |
- |
- |
- |
- |
- |
125 |
- |
130 |
- |
2 Treated for solution treatment
3 Treated for solution treatment and cold working
4 Treated for solution treatment and age hardening
5 Treated for solution treatment, cold working and age hardening |
|
Mechanical properties of wrought and raw bars for die forging
(EN 12165) : |
State |
Nominal size of the straight section |
Hardness |
Tensile strength
Rm
N/mm˛
approx. |
Conventional elastic limit at 0,2 %
Rp0,2
N/mm˛
approx. |
Stretching
A%
approx. |
Diameter
mm |
Size on flat mm |
from |
until and included |
from |
until and included |
HB
min. |
HV
min. |
M |
All sizes |
|
|
|
|
|
H0502 |
6 |
80 |
6 |
60 |
50 |
50 |
(300) |
(200) |
(20) |
H1203 |
120 |
125 |
(440) |
(300) |
(15) |
2 Without age hardening
3 With age hardening |
|
Mechanical properties of wires (EN 12166) : |
State |
Diameter |
Tensile strength Rm N/mm˛ |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching |
Hardness
HV |
from |
more than |
until |
min. |
Max. |
A100mm
% min. |
A11,3
% min. |
A
% min. |
min. |
max. |
M |
All sizes |
- |
- |
- |
- |
- |
- |
- |
- |
R4504 |
1,5 |
- |
6,0 |
450 |
- |
(440) |
5 |
6 |
- |
- |
- |
H1354 |
1,5 |
- |
6,0 |
- |
- |
- |
- |
- |
- |
135 |
175 |
R4104 |
- |
6,0 |
15,0 |
410 |
- |
(400) |
- |
6 |
8 |
- |
- |
H1204 |
- |
6,0 |
15,0 |
- |
- |
- |
- |
- |
- |
120 |
160 |
R6506 |
1,5 |
- |
6,0 |
650 |
- |
(620) |
7 |
8 |
- |
- |
- |
H1906 |
1,5 |
- |
6,0 |
- |
- |
- |
- |
- |
- |
190 |
240 |
R5906 |
- |
6,0 |
15,0 |
590 |
- |
(580) |
7 |
8 |
10 |
- |
- |
H1706 |
- |
6,0 |
15,0 |
- |
- |
- |
- |
- |
- |
170 |
220 |
4
Treated for solution treatment and cold working
6
Treated for solution treatment, cold working and age hardening |
|
Mechanical properties of sections and rectangular bars (EN 12167): |
State |
Sizes |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching
A % |
Hardness |
Section |
Rectangular bars thickness mm |
>
at |
<
or = |
HB
min. |
HV
min |
M
|
All |
All |
|
|
|
|
|
R2505
|
-
|
3
|
60
|
250
|
(100)
|
(35)
|
-
|
-
|
H0605 |
- |
3 |
60 |
- |
- |
- |
60 |
65 |
R3802 |
- |
3 |
60 |
380 |
(250) |
(8) |
- |
- |
H1102 |
- |
3 |
60 |
- |
- |
- |
110 |
115 |
R4203 |
- |
3 |
30 |
420 |
(260) |
(15) |
- |
- |
H1203 |
- |
3 |
30 |
- |
- |
- |
120 |
125 |
R5604 |
- |
3 |
30 |
560 |
(520) |
(10) |
- |
- |
H1704 |
- |
3 |
30 |
- |
- |
- |
170 |
180 |
2
Treated for solution treatment and cold working
3
Treated for solution treatment and precipitation hardening
4
Treated for solution treatment, cold working and precipitation hardening
5 Treated for solution treatment |
|