The bronzes of aluminum have a high resistance combined with a good oxidation and corrosion resistances, in particular in the sea environments.
|
Chemical compound % |
Agent |
Cu |
Al |
Fe |
Mn |
Ni |
Pb |
Si |
Sn |
Zn |
Zr |
Other |
Mass-volume g/cm3 |
Mini: |
Reste
|
6,0
|
0,5
|
-
|
-
|
-
|
2,0
|
-
|
-
|
-
|
-
|
7,7
|
Maxi: |
-
|
6,4
|
0,7
|
0,1
|
0,1
|
0,05
|
2,4
|
0,1
|
0,4
|
-
|
0,2
|
|
|
Mechanical properties of bars for general usings (EN 12163) : |
State |
Implementation |
Diameter or size/flats mm |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2 Rp0,2 N/mm² |
Stretching |
Hardness |
from |
more than |
until |
A100mm
% min. |
A11,3
% min. |
A
% min. |
HB
min. |
HB
max. |
HV
min. |
HV
max. |
M
|
|
5
|
-
|
80
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
R500
|
|
5
|
-
|
80
|
500
|
(250)
|
-
|
18
|
20
|
-
|
-
|
-
|
-
|
H120 |
|
5 |
- |
80 |
- |
- |
- |
- |
- |
120 |
150 |
125 |
155 |
R600 |
|
5 |
- |
40 |
600 |
(350) |
- |
10 |
12 |
- |
- |
- |
- |
H140 |
|
5 |
- |
40 |
- |
- |
- |
- |
- |
140 |
- |
145 |
- |
|
Mechanical properties of wrought and raw bars for die forging (EN 12165) : |
State |
Nominal size of the straight section |
Hardness |
Tensile strength
Rm
N/mm˛
approx. |
Conventional elastic limit at 0,2 %
Rp0,2
N/mm˛
approx. |
Stretching
A%
approx. |
Diameter
mm |
Size on flat mm |
from |
until and included |
from |
until and included |
HB
min. |
HV
min. |
M |
All sizes |
|
|
|
|
|
H120 |
6 |
80 |
6 |
60 |
120 |
125 |
(500) |
(250) |
(20) |
|
Mechanical properties of sections and rectangular bars (EN 12167): |
State |
Sizes |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching
A % |
Hardness |
Section |
Rectangular bars thickness mm |
>
at |
<
or = |
HB
min. |
HV
min |
M
|
All |
All |
|
|
|
|
|
R550
|
-
|
-
|
6
|
550
|
(300)
|
(10)
|
-
|
-
|
H140 |
- |
- |
6 |
- |
- |
- |
140 |
145 |
R500 |
- |
6 |
60 |
500 |
(250) |
(20) |
- |
- |
H120 |
- |
6 |
60 |
- |
- |
- |
120 |
125 |
|