Chemical compound % |
Agent: |
Cu |
Fe |
Mn |
Ni |
Pb |
Sn |
Zn |
Other |
Mass-volume g/cm3 |
Mini: |
47,0
|
-
|
1,5
|
6,0
|
2,3
|
-
|
Reste
|
-
|
8,5 |
Maxi: |
50,0
|
0,3
|
3,0
|
8,0
|
3,3
|
0,2
|
-
|
0,2
|
|
Mechanical properties of bars for screw cutting (EN 12164) : |
State |
Nominal size of the straight section |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching |
Hardness
HB
or HV
approx |
Diameter
mm |
Size on flat mm |
from |
until and included |
from |
until and included |
A100mm
% min. |
A11,3
% min. |
A
% min. |
M |
2 |
50 |
2 |
40 |
|
|
|
|
|
|
R510 |
2 |
50 |
2 |
40 |
510 |
(400) |
8 |
10 |
12 |
(150) |
R590 |
2 |
20 |
2 |
16 |
590 |
(500) |
(2) |
(3) |
5 |
(170) |
R680 |
2 |
5 |
2 |
5 |
680 |
(600) |
- |
- |
- |
(200) |
|
Mechanical properties of wrought and raw bars for die forging
(EN 12165) : |
State |
Nominal size of the straight section |
Hardness |
Tensile strength
Rm
N/mm˛
approx. |
Conventional elastic limit at 0,2 %
Rp0,2
N/mm˛
approx. |
Stretching
A%
approx. |
Diameter
mm |
Size on flat mm |
from |
until and included |
from |
until and included |
HB
min. |
HV
min. |
M |
All sizes |
|
|
|
|
|
H110 |
6 |
80 |
6 |
60 |
110 |
115 |
(460) |
(250) |
(12) |
|
Mechanical properties of wires (EN 12166) : |
State |
Diameter |
Tensile strength Rm N/mm˛ |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching |
Hardness
HV |
from |
more than |
until |
min. |
Max. |
A100mm
% min. |
A11,3
% min. |
A
% min. |
min. |
max. |
M |
1,5 |
- |
12,0 |
- |
- |
- |
- |
- |
- |
- |
- |
R520 |
1,5 |
- |
12,0 |
520 |
- |
(250) |
12 |
15 |
18 |
- |
- |
H130 |
1,5 |
- |
12,0 |
- |
- |
- |
- |
- |
- |
130 |
170 |
R620 |
1,5 |
- |
10,0 |
620 |
- |
(500) |
(3) |
5 |
7 |
- |
- |
H160 |
1,5 |
- |
10,0 |
- |
- |
- |
- |
- |
- |
160 |
200 |
R700 |
1,5 |
- |
5,0 |
700 |
- |
(620) |
- |
- |
- |
- |
- |
H190 |
1,5 |
- |
5,0 |
- |
- |
- |
- |
- |
- |
190 |
230 |
|
Mechanical properties of sections and rectangular bars (EN 12167): |
State |
Sizes |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching
A % |
Hardness |
Section |
Rectangular bars thickness mm |
>
at |
<
or = |
HB
min. |
HV
min |
M
|
All |
All |
|
|
|
|
|
R650
|
-
|
-
|
6
|
650
|
(450)
|
(5)
|
-
|
-
|
H170 |
- |
- |
6 |
- |
- |
- |
170 |
180 |
R600 |
- |
6 |
60 |
600 |
(400) |
(8) |
- |
- |
H150 |
- |
6 |
60 |
- |
- |
- |
150 |
155 |
|