Suitable to the hot working. Limited ductility at ambient temperature.
|
Chemical compound % |
Agent |
Cu |
Al |
Fe |
Ni |
Pb |
Sn |
Zn |
Other |
Mass-volume g/cm3 |
Mini: |
59,5
|
-
|
-
|
-
|
-
|
-
|
Reste
|
-
|
8,4 |
Maxi: |
61,5
|
0,05
|
0,2
|
0,3
|
0,3
|
0,2
|
-
|
0,2
|
|
Mechanical properties of forged parts (EN 12420) : |
State |
Hardness
HB min. |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² min. |
Stretching
A % min. |
H075
|
75
|
(340)
|
(100)
|
(25)
|
|
Mechanical properties of plates, sheets and coils for general usings (EN1652) : |
State |
Thickness |
Tensile strength Rm N/mm˛ |
Conventional elastic limit at 0,2 Rp0,2 N/mm² . |
Stretching |
Hardness
HV |
From |
to |
min. |
max. |
A50mm
ep < or = 2,5 |
A
ep > 2,5 |
min. |
max. |
R340
|
0,3
|
10
|
340
|
420
|
(max.
240) |
33
|
43
|
-
|
-
|
H085
|
0,3
|
10
|
-
|
- |
-
|
-
|
-
|
85
|
115
|
R400 |
0,3 |
10 |
400 |
480 |
(min.
200) |
15 |
23 |
- |
- |
H110 |
0,3 |
10 |
- |
- |
- |
- |
- |
110 |
140 |
R470 |
0,3 |
5 |
470 |
- |
(min.
390) |
6 |
12 |
- |
- |
H140 |
0,3 |
5 |
- |
- |
- |
- |
- |
140 |
- |
|
Mechanical properties of bars for general usings (EN 12163) : |
State |
Implementation |
Diameter or size/flats mm |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2 Rp0,2 N/mm² |
Stretching |
Hardness |
from |
more than |
until |
A100mm
% min. |
A11,3
% min. |
A
% min. |
HB
min. |
HB
max. |
HV
min. |
HV
max. |
M
|
|
2
|
-
|
80
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
R340
|
|
2
|
-
|
80
|
340
|
(260)
|
18
|
20
|
25
|
-
|
-
|
-
|
-
|
H080 |
|
2 |
- |
80 |
- |
- |
- |
- |
- |
80 |
- |
85 |
- |
|
Mechanical properties of bars for die forging (EN 12165) : |
State |
Nominal size of the straight section |
Hardness |
Tensile strength
Rm
N/mm˛
approx. |
Conventional elastic limit at 0,2 %
Rp0,2
N/mm˛
approx. |
Stretching
A%
approx. |
Diameter
mm |
Size on flat mm |
from |
until and included |
from |
until and included |
HB
min. |
HV
min. |
M |
All sizes |
|
|
|
|
|
H070 |
6 |
80 |
6 |
60 |
70 |
75 |
(300) |
(100) |
(20) |
|
Mechanical properties of sections and rectangular bars (EN 12167): |
State |
Sizes |
Tensile strength Rm N/mm² min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching A % |
Hardness |
Section |
Rectangular bars thickness mm |
>
at |
<
or = |
HB
min. |
HV
min |
M
|
All |
All |
|
|
|
|
|
R440
|
-
|
-
|
6
|
440
|
(300)
|
(10)
|
-
|
-
|
H120 |
- |
- |
6 |
- |
- |
- |
120 |
125 |
R400 |
- |
6 |
60 |
400 |
(190) |
(18) |
- |
- |
H100 |
- |
6 |
60 |
- |
- |
- |
100 |
105 |
|
Average physical and mechanical properties (for information only): |
Average physical properties: |
Liquidus temperature (°C) |
Solidus temperature (°C) |
Solidification range (°C) |
Mass-volume at 20°C (kg/dm3) |
Linear expansion coefficient (10-6/°C) |
905 |
900 |
5 |
8,39 |
21 |
Massive heat capacity at 20°C (J/kg.K) |
Heat conductivity at 20°C (W/m.K) |
Electrical conductivity at 20°C (%IACS) |
Electrical resistivity at 20° C (10-8 W.m) |
Coefficient of resistivity temperature from 0 to 100°C (10-3°C) |
376 |
121 |
28 |
6,2 |
2 |
Average mechanical properties: |
Young's modulus (MPA) |
Modulus of twisting (MPA) |
Poisson's ratio |
Annealing |
Strain aging |
Annealing |
Strain aging |
102000 |
94000 |
37000 |
35000 |
±
0,35 |
|