Composition
chimique des cuivres et alliages selon la DIN : |
|
Cuivres
purs et faiblement alliés corroyés
|
Designation |
Composition,
en pourcentage (fourchette ou maxi) |
|
Numérique |
Cu |
Ag |
Cd |
Fe |
Mg |
Mn |
Si |
P |
Pb |
Autres, |
E-Cu58 |
2.0065 |
99.90 |
- |
- |
- |
- |
- |
- |
- |
- |
O
0.005- |
0.040 |
E-Cu57 |
2.0060 |
99.90 |
- |
- |
- |
- |
- |
- |
- |
- |
O
0.005- |
0.040 |
OF-Cu |
2.004 |
99.95 |
- |
SE-Cu |
2.0070 |
99.90 |
- |
SW-Cu |
2.0076 |
99.90 |
- |
SF-Cu |
2.0090 |
99.90 |
- |
0.003 |
- |
CuAg0.03 |
2.1202 |
Solde |
0.025- |
– |
– |
– |
– |
– |
0.005- |
– |
0.05,
O, |
0.050 |
0.014 |
0.04 |
CuAg0.1 |
2.1203 |
Solde |
0.08- |
– |
– |
– |
– |
– |
0.015- |
– |
0.05,
O, |
0.12 |
0.040 |
0.04 |
CuAg0.1P |
2.1191 |
Solde |
0.08- |
– |
– |
– |
– |
– |
0.001-0.007 |
– |
0.05 |
0.12 |
CuAsP,
(SB-Cu) |
2.1202 |
Solde |
0.025- |
– |
– |
– |
– |
– |
0.015- |
– |
0.25, |
0.050 |
0.40 |
As
0.15-0.5 |
CuCd0.5 |
2.1265 |
Solde |
– |
0.3-0.8 |
– |
– |
– |
– |
– |
– |
0.3 |
CuCd1 |
2.1266 |
Solde |
– |
0.9-1.3 |
– |
– |
– |
– |
– |
– |
0.3 |
CuCdSn |
2.1270 |
Solde |
– |
0.2-0.8 |
– |
– |
– |
– |
– |
– |
0.5,
Sn 0.2-0.8 |
CuMg0.4 |
2.1322 |
|
– |
– |
– |
0.3-0.5 |
– |
– |
– |
– |
0.3 |
CuMg0.7 |
2.1323 |
|
– |
– |
– |
0.5- |
– |
– |
– |
– |
0.3 |
0.8 |
CuMn2 |
2.1363 |
Solde |
– |
– |
0.1 |
– |
1.5- |
– |
– |
0.03 |
0.5,
0.2 Zn |
2.0 |
CuMn5 |
2.1366 |
Solde |
– |
– |
0.1 |
– |
4.0-5.0 |
– |
– |
0.03 |
0.5,
0.2 Zn |
CuSi3Mn |
2.1525 |
Solde |
– |
– |
0.25 |
– |
0.5- |
2.7-3.6 |
– |
0.05 |
0.5,
0.2 Zn |
1.3 |
CuSi2Mn |
2.1522 |
|
– |
– |
0.25 |
– |
0.3-0.7 |
0.8-2.2 |
– |
0.05 |
0.5,
0.2 Zn |
CuSP |
2.1498 |
Solde |
– |
– |
– |
– |
– |
– |
0.005- |
– |
0.10,
S 0.3-0.5 |
0.012 |
CuTeP,
(SF-CuTe) |
2.1546 |
Solde |
– |
– |
– |
– |
– |
– |
0.005- |
– |
0.05,
0.7Te |
0.012 |
CuPb1P |
2.116 |
Solde |
- |
- |
- |
- |
- |
- |
0.003- |
0.7-1.5 |
0.1 |
0.012 |
CuZn0.5 |
2.0205 |
Solde |
- |
0.02 |
- |
0.2,
Zn 0.1-1.0 |
CuFe2P |
2.131 |
- |
- |
- |
2.1-2.6 |
- |
- |
- |
0.015- |
0.03 |
0.5,
Zn 0.05- |
0.15 |
0.20 |
|
Retour haut de page |
Cuivres
purs et faiblement alliés coulés |
Designation |
Composition,
en pourcentage (fourchette ou maxi) |
|
Numérique |
Cu |
Ag |
Cd |
Fe |
Mg |
Mn |
Si |
P |
Pb |
Autres, |
G-CuL35 |
2.0109 |
98
min. |
- |
- |
- |
- |
- |
- |
- |
- |
- |
GK-CuL35 |
G-CuL45 |
2.0082 |
99.6
min |
- |
- |
- |
- |
- |
- |
- |
- |
- |
GKCuL45 |
G-CuL50 |
2.0085 |
99.7
min. |
- |
- |
- |
- |
- |
- |
- |
- |
- |
GK-CuL50 |
2.0075 |
|
Retour
haut de page |
Cuivres
purs et faiblement alliés subissant un traitement |
Designation |
Composition,
en pourcentage (fourchette ou maxi) |
|
Numérique |
Cu |
Be |
Co |
Cr |
Fe |
Ni |
Ni+Co |
Si |
Autres,
Total |
CuBe1.7 |
2.1245 |
Solde |
1.6-1.8 |
Ni+Co+Fe
0.6 |
- |
Ni+Co+Fe
0.6 |
- |
0.2-0.6 |
- |
CuBe2 |
2.1247 |
Solde |
1.8-2.1 |
Ni+Co+Fe
0.6 |
- |
Ni+Co+Fe
0.6 |
- |
0.2-0.6 |
- |
0.5 |
CuBe2Pb |
2.1248 |
Solde |
1.8-2.1 |
Ni+Co+Fe
0.6 |
- |
0.2-0.6 |
- |
0.5,
Pb 0.2-0.5 |
CuCo2Be |
2.1285 |
Solde |
0.4-0.7 |
2.0-2.8 |
- |
Ni+Fe
0.5 |
Ni+Fe
0.5 |
- |
0.5 |
CuNi2Be |
2.0850 |
Solde |
0.2-0.6 |
- |
1.4-2.0 |
- |
0.5 |
CuNi1.5Si |
2.0853 |
Solde |
- |
1.0-1.6 |
- |
0.4-0.7 |
0.5 |
CuNi2Si |
2.0855 |
Solde |
- |
1.6-2.5 |
- |
0.5-0.8 |
0.5 |
CuNi3Si |
2.0857 |
Solde |
- |
2.6-4.5 |
- |
0.8-1.3 |
0.6 |
CuCr |
2.1252 |
Solde |
- |
0.4-1.2 |
- |
Zn
0.2, Cd 0.5 |
CuCrZr |
2.1293 |
Solde |
– |
– |
0.3-1.2 |
– |
|
– |
|
0.2,
Zr 0.03-0.3 |
CuZr |
2.158 |
Solde |
- |
0.2,
Zr 0.1-0.3 |
CuCrZr |
2.1291 |
- |
0.3-1.2 |
- |
0.3 |
Cuivre-Chrome
coulé |
G-CuCrF35 |
2.1292 |
Solde |
- |
0.4-1.2 |
- |
Zn
0.2, Cd 0.5 |
|
Retour haut
de page |
Laitons |
Designation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
|
Ancienne
Designation |
Cu |
Zn |
Al |
Fe |
Ni |
Pb |
Sn |
Autres, |
Cuivre
Zinc binaire |
CuZn5 |
2.0220 |
Ms95 |
94.0-96.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn10 |
2.0230 |
Ms90 |
89.0-91.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn15 |
2.0240 |
Ms85 |
84.0-86.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn20 |
2.0250 |
Ms80 |
79.0-81.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn28 |
2.0261 |
Ms72 |
71.0-73.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn30 |
2.0265 |
Ms70 |
69.0-71.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn33 |
2.0280 |
Ms67 |
66.0-68.5 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn36 |
2.0335 |
Ms63 |
63.5-65.0 |
Solde. |
0.02 |
0.05 |
0.2 |
0.05 |
0.05 |
0.1 |
CuZn37 |
2.0321 |
Ms63 |
62.0-64.0 |
Solde. |
0.03 |
0.1 |
0.3 |
0.1 |
0.1 |
0.1 |
CuZn40 |
2.0360 |
Ms60 |
59.5-61.5 |
Solde. |
0.05 |
0.2 |
0.3 |
0.3 |
0.2 |
0.2 |
Cuivre
Zinc Plomb |
CuZn36Pb1.5 |
2.0331 |
Ms63Pb |
62.0-64.0 |
Solde. |
0.05 |
0.2 |
0.3 |
0.7-2.5 |
0.1 |
0.1 |
CuZn37Pb0.5 |
2.0332 |
Ms63Pb |
62.0-64.0 |
Solde. |
0.05 |
0.2 |
0.3 |
0.1-0.7 |
0.1 |
0.1 |
CuZn36Pb3 |
2.0375 |
– |
60.0-62.0 |
Solde. |
0.05 |
0.3 |
0.3 |
2.5-3.5 |
0.2 |
0.2 |
CuZn38Pb1.5 |
2.0371 |
Ms60Pb |
59.5-61.5 |
Solde. |
0.05 |
0.3 |
0.3 |
1.0-2.0 |
0.2 |
0.2 |
CuZn39Pb0.5 |
2.0372 |
Ms60Pb |
59.5-61.5 |
Solde. |
0.05 |
0.3 |
0.3 |
0.3-1.5 |
0.2 |
0.2 |
CuZn39Pb2 |
2.0380 |
Ms58 |
58.5-60.0 |
Solde. |
0.1 |
0.4 |
0.3 |
1.5-2.5 |
0.2 |
0.2 |
CuZn39Pb3 |
2.0401 |
Ms58 |
57.0-59.0 |
Solde. |
0.1 |
0.5 |
0.5 |
2.5-3.5 |
0.4 |
0.2 |
CuZn40Pb2 |
2.0402 |
Ms58 |
57.0-59.0 |
Solde. |
0.1 |
0.4 |
0.4 |
1.5-2.5 |
0.3 |
0.2 |
CuZn44Pb2 |
2.0410 |
Ms56 |
54.0-56.0 |
Solde. |
0.5 |
0.5 |
0.5 |
1.0-2.5 |
0.4 |
0.4 |
Laitons
coulés |
G-CuZn33Pb |
2.028 |
G-Ms65 |
63-67 |
Solde |
|
1 |
1-3 |
|
2.0 |
G-CuZn37Pb0.5 |
2.034 |
G-Ms60 |
59-63 |
Solde |
0.2-0.8 |
|
1 |
0.5-2.5 |
|
1.2 |
G-CuZn15 |
2.0241 |
|
83-87.5 |
Solde |
|
|
0.2 |
0.5 |
0.5 |
0.8, |
As
O.05- |
0.20 |
|
Retour
haut de page |
Laitons
complexes : |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
|
Numérique |
Ancienne
Designation |
Cu |
Zn |
Al |
As |
Fe |
Mg |
Mn |
Ni |
Si |
Sn |
P |
Pb |
Autres, |
CuZn20Al2 |
2.0460 |
SoMs76 |
70.0- |
Solde |
1.8-2.3 |
0.020- |
0.07 |
0.005 |
0.1 |
0.1 |
– |
– |
0.01 |
0.07 |
0.1 |
2.5 |
0.035 |
CuZn23Al6 |
2.0500 |
SoMs64 |
63.0- |
Solde |
5.0-7.0 |
– |
2.0- |
– |
3.5- |
0.5 |
– |
– |
– |
1.0 |
0.2 |
65.5 |
3.5 |
5.0 |
CuZn28Sn1 |
2.0470 |
SoMs71 |
70.0- |
Solde. |
– |
0.020- |
0.07 |
– |
0.1 |
0.1 |
– |
0.9- |
0.01 |
0.07 |
0.1 |
72.5 |
0.035 |
1.3 |
CuZn31Si1 |
2.0490 |
SoMs68 |
66.0- |
Solde. |
– |
– |
0.4 |
– |
– |
0.5 |
0.7- |
– |
– |
0.8 |
0.5 |
70.0 |
1.3 |
CuZn35Ni2 |
2.0540 |
SoMs59 |
58.0- |
Solde. |
0.3- |
– |
0.5 |
– |
1.5- |
2.0- |
0.1 |
0.5 |
– |
0.8 |
0.5 |
61.0 |
1.5 |
2.5 |
3.0 |
CuZn38SnAl |
2.0525 |
SoMs58Al |
59.0- |
Solde. |
0.1-0.5 |
0.05 |
0.1- |
– |
– |
0.2- |
– |
0.3- |
– |
0.3- |
0.5 |
60.7 |
0.4 |
0.5 |
0.6 |
0.7 |
CuZn38Sn1 |
2.0530 |
|
59.0- |
Solde. |
– |
– |
0.1 |
– |
– |
0.2 |
– |
0.5- |
– |
0.2 |
0.5 |
62.0 |
1.0 |
CuZn37Al1 |
2.0510 |
SoMs58Al |
59.0- |
Solde. |
0.3- |
– |
1.0 |
– |
0.6- |
0.6 |
0.5 |
0.3 |
– |
1.0 |
0.5 |
61.5 |
1.3 |
1.6 |
CuZn40Al1 |
2.0561 |
SoMs58Al |
57.5- |
Solde. |
0.4- |
– |
1.0 |
– |
0.8- |
1.0 |
0.7 |
0.4 |
– |
0.8 |
0.5 |
60.0 |
1.3 |
1.8 |
CuZn40Al2 |
2.0550 |
SoMs58Al2 |
56.5- |
Solde. |
1.3- |
– |
1.0 |
– |
1.4- |
2.0 |
0.3- |
0.5 |
– |
0.8 |
0.5 |
59.0 |
2.3 |
2.6 |
1.0 |
CuZn40Mn2 |
2.0572 |
SoMs58 |
57.0- |
Solde. |
0.1 |
– |
1.5 |
– |
1.0- |
1.0 |
0.1 |
0.5 |
– |
|
59.0 |
2.5 |
|
Laitons
complexes coulés : |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
|
Ancienne
Designation |
Cu |
Zn |
Al |
As |
Fe |
Mg |
Mn |
Ni |
Si |
Sn |
P |
Pb |
Autres,
Total |
G-CuZn15Si4 |
2.0492 |
- |
78-83 |
Solde. |
- |
0.6 |
- |
1 |
3.8-5 |
- |
1.2 |
G-CuZn25Si4 |
2.0598 |
G-SoMsF75 |
60-67 |
Solde |
3-7 |
- |
1.5-4 |
- |
2.5-5 |
3 |
- |
0.5 |
G-CuZn34Al2 |
2.0596 |
G-SoMsF60 |
55-66 |
Solde |
1-3 |
- |
0.5-2.5 |
- |
0.3-4 |
3 |
- |
0.5 |
G-CuZn35Al1 |
2.0592 |
G-SoMsF45 |
56-65 |
Solde |
0.502 |
- |
0.5-2 |
- |
0.3-3 |
2 |
- |
1.5 |
G-CuZn37Al1 |
2.0585 |
G-SoMsF45 |
60-64 |
Solde |
0.3-1.8 |
- |
2 |
- |
1.5 |
G-CuZn38Al |
2.0531 |
G-Ms60 |
59-64 |
Solde |
0.1-0.8 |
- |
1 |
- |
1.2 |
G-CuZn40Fe |
2.0590 |
G-SoMsF30 |
56-62 |
Solde |
- |
0.2-1.2 |
- |
2.5 |
2 |
- |
1 |
|
1.2 |
|
Retour
haut de page |
Bronzes
corroyés |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
|
Ancienne
Designation |
Cu |
Zn |
Fe |
Ni |
P |
Pb |
Sn |
Autres, |
CuSn2 |
2.1010 |
SnBz2 |
Solde |
0.3 |
0.1 |
0.2 |
0.01-0.35 |
0.05 |
1.0-2.5 |
0.1 |
CuSn4 |
2.1016 |
SnBz4 |
Solde |
0.3 |
0.1 |
0.3 |
0.01-0.35 |
0.05 |
3.5-4.5 |
0.2 |
CuSn6 |
2.1020 |
SnBz6 |
Solde |
0.3 |
0.1 |
0.3 |
0.01-0.35 |
0.05 |
5.5-7.5 |
0.2 |
CuSn8 |
2.1010 |
SnBz8 |
Solde |
0.3 |
0.1 |
0.3 |
0.01-0.35 |
0.05 |
7.5-9.0 |
0.2 |
CuSn6Zn |
2.1010 |
MSnBz6 |
Solde |
5.0-7.0 |
0.1 |
0.3 |
0.01-0.1 |
0.05 |
5.0-7.0 |
0.2 |
|
Retour
haut de page |
Bronzes
coulés : |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
Numérique |
Cu |
Sn |
Pb |
Zn |
P |
Ni |
Sb |
Fe |
S |
Autres
, Total |
G-SnBz
20 |
- |
78-80 |
20-22 |
– |
– |
– |
- |
G-SnBz
14 |
- |
85-87 |
13-15 |
– |
– |
– |
- |
G-SnBz
12 |
- |
87-89 |
11-13 |
– |
– |
– |
- |
- |
- |
- |
- |
G-SnBz
10 |
- |
89-91 |
9-11 |
– |
– |
– |
|
Rg6 |
- |
85 |
6 |
2 |
3 |
|
1 |
- |
Rg
4 |
- |
92-94 |
3-5 |
1-2 |
2 |
– |
- |
Rg2 |
- |
83 |
2 |
8 |
5 |
- |
Rg
A |
- |
81-87 |
5-8 |
4-6 |
7 |
– |
|
G-PbBz
25 |
2.1166 |
Solde. |
3 |
18-28 |
3 |
0.05 |
2.5 |
0.5 |
0.7 |
- |
1 |
G-SnPbBz
22 |
- |
Solde. |
2-5 |
18-25 |
– |
– |
- |
G-CuPb5Sn |
2.1170 |
84-87 |
9-11 |
4-6 |
0-2 |
0.05 |
0-2 |
0.35 |
0.25 |
- |
0.5 |
G-SnPbBz
5 |
2.1170 |
Solde. |
9-11 |
3-7 |
– |
– |
- |
G-CuPb10Sn |
2.1176 |
78-82 |
9-11 |
8-11 |
0-2 |
0.05 |
0-1.5 |
0.5 |
0.25 |
- |
0.5 |
G-SnPbBz
10 |
2.1176 |
Solde. |
9-11 |
8-12 |
– |
– |
- |
G-CuPb15Sn |
2.1182 |
76-79 |
7-9 |
13-17 |
0-3 |
0.05 |
0-2 |
0.50 |
0.25 |
- |
0.5 |
G-SnPbBz
15 |
2.1182 |
Solde. |
6-8 |
13-18 |
3 |
0.05 |
2 |
0.5 |
0.25 |
- |
0.5 |
G-CuPb20Sn |
2.1188 |
69-76 |
4-6 |
18-23 |
0-3 |
0.05 |
0-2.5 |
0.60 |
0.25 |
- |
0.5 |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
Numérique |
Cu |
Sn |
Pb |
Zn |
P |
Ni |
Sb |
Fe |
S |
Autres
, Total |
G-SnPbBz20 |
2.1188 |
69.0-77.0 |
3.5-5.5 |
18.0-23.0 |
3.0 |
0.05 |
2.5 |
0.50 |
0.25 |
- |
0.5 |
G-CuPb22Sn |
2.1166 |
70-80 |
0.5-3 |
18-26 |
0-0.5 |
0.03 |
0-2.5 |
0.20 |
0.7 |
- |
1.2 |
G-CuSn10Zn |
2.1086 |
86-89 |
9-11 |
0-1.5 |
1-3 |
0.05 |
0-2 |
0.3 |
0.25 |
0.1 |
0.5 |
Rg
10, |
2.1086 |
85-87 |
9-11 |
– |
4 |
– |
- |
- |
- |
- |
- |
GZ-RG
10 |
G-CuSn2ZnPb |
2.1098 |
80-85 |
1.5-3 |
4-6 |
7-9 |
0.05 |
1.5-2.5 |
0.25 |
0.30 |
0.1 |
0.5 |
G-CuSn5ZnPb |
2.1096 |
84-86 |
4-6 |
4-6 |
4-6 |
0.05 |
0-2.5 |
0.3 |
0.30 |
0.1 |
0.5 |
Rg
5, |
2.1096 |
84-86 |
4-6 |
4-6 |
4-6 |
– |
- |
- |
- |
- |
- |
GZ-RG
5 |
G-CuSn6ZnNi |
2.1093 |
83.5-87.5 |
5.5-7 |
2.5-4 |
1.5-3 |
0.05 |
1.5-2.5 |
0.3 |
0.25 |
0.05 |
0.5 |
G-CuSn7ZnPb |
2.1090 |
81-86 |
6-8 |
5-7 |
3-5 |
0.05 |
0-2 |
0.3 |
0.25 |
0.1 |
0.5 |
Rg7 |
2.1090 |
83-85 |
6-8 |
3-5 |
3-5 |
- |
G-CuSn10 |
2.1050 |
88-90 |
9-11 |
0-1 |
|
0.2 |
0-2 |
0.2 |
- |
G-CuSn12Pb |
2.1061 |
84-87 |
11-13 |
1-2 |
- |
0.2 |
0-2 |
0.2 |
- |
G-CuSn12 |
2.1052 |
84-88.5 |
11-13 |
0-1 |
0-1 |
0.4 |
0-2 |
0.2 |
- |
G-CuSn12Ni |
2.1060 |
84-87 |
11-13 |
0-0.3 |
- |
0.2 |
1.5-2.5 |
0.1 |
- |
|
Retour
haut de page |
Cupro-aluminiums
: |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
|
Ancienne
Designation |
Cu |
Zn |
Al |
As |
Fe |
Mn |
Ni |
Pb |
Si |
Sn |
Autres
, Total |
Produits
corroyés |
CuAl5 |
2.0916 |
AlBz5 |
92.5-96 |
0.5 |
4.0-6.0 |
0.4 |
0.4 |
0.3 |
0.8 |
0.02 |
0.2 |
0.3 |
0.3 |
CuAl5As |
2.0918 |
AlBz5 |
Solde |
0.3 |
4.0-6.0 |
0-0.2 |
0.2 |
0.2 |
0.2 |
0.02 |
|
– |
0.3 |
CuAl8 |
2.092 |
AlBz8 |
Solde |
0.5 |
7.0-9.0 |
– |
0.5 |
0.8 |
0.8 |
0.02 |
0.2 |
– |
0.3 |
CuAl8Fe |
2.0932 |
AlBz8Fe |
Solde |
0.5 |
6.5-9.0 |
– |
1.5-3.5 |
1.0 |
1.0 |
0.15 |
0.2 |
0.2 |
0.3 |
CuAl9Fe3Mn2 |
2.0936 |
AlBz10Fe |
Solde |
0.5 |
9.0-11.0 |
– |
2.0-4.0 |
1.5-3.5 |
1.0 |
0.05 |
0.2 |
– |
0.3 |
CuAl9Mn |
2.096 |
AlBz9Mn |
Solde |
0.5 |
8-10 |
– |
1.5 |
1.5-3.0 |
0.8 |
0.15 |
0.2 |
– |
0.3 |
CuAl10Ni5Fe4 |
2.0966 |
AlBz10Ni |
Solde |
0.5 |
8.5-11 |
– |
2.5-5.3 |
1.5 |
4.0-6.0 |
0.15 |
0.2 |
– |
0.3 |
CuAl11Ni6Fe5 |
2.0978 |
AlBz11Ni |
Solde |
0.5 |
10.5-12.5 |
– |
4.8-7.3 |
1.5 |
5.0-7.5 |
0.15 |
0.2 |
– |
0.3 |
Produits
coulés |
G-CuAl10Fe |
2.0940 |
G-FeAlBzF50 |
83min |
- |
8-11 |
- |
2-4 |
1 |
3 |
- |
1.0 |
G-CuAl9Ni |
2.0970 |
G-FeAlBzF50 |
82min |
- |
8.5-10 |
- |
1-3 |
2.5 |
1.5-4 |
- |
0.8 |
G-CuAl10Ni |
2.0975 |
G-FeAlBzF70 |
76min |
- |
8.5-11 |
- |
3.5-5.5 |
3 |
4-6.5 |
- |
0.8 |
G-CuAl11Ni |
2.0980 |
G-FeAlBzF68 |
73min |
- |
9-12.3 |
- |
4-7 |
2.5 |
5-7.5 |
- |
0.8 |
G-CuAl8Mn |
2.0962 |
G-FeAlBzF42 |
82min |
- |
7-9 |
- |
6.5 |
1-2 |
- |
0.8 |
|
Retour
haut de page |
Cupro
Nickel Zinc |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
|
Designation |
Cu |
Zn |
Fe |
Mn |
Ni |
Pb |
Sn |
Autres
, Total |
CuNi7Zn39Mn5Pb3 |
2.0771 |
- |
44-48 |
Solde |
0.3 |
0.5 |
9.0-11.0 |
0.5-2.0 |
- |
0.4 |
CuNi10Zn42Pb |
2.0770 |
Ns4711Pb |
45.0-48.0 |
Solde |
0.5 |
0.5 |
9.0-11.0 |
0.5-2.0 |
0.3 |
0.1 |
CuNi12Zn24 |
2.0730 |
Ns6512 |
63.0-66.0 |
Solde |
0.3 |
0.5 |
11.0-13.0 |
0.03 |
0.3 |
0.2 |
CuNi12Zn30Pb |
2.0780 |
Ns5712Pb |
56.0-58.0 |
Solde |
0.3 |
0.7 |
11.0-13.0 |
0.3-1.5 |
0.3 |
0.4 |
CuNi18Zn20 |
2.0740 |
Ns6218 |
60.0-63.0 |
Solde |
0.3 |
0.5 |
17.0-19.0 |
0.03 |
0.2 |
0.2 |
CuNi18Zn19Pb |
2.0790 |
Ns6218Pb |
59.0-63.0 |
Solde |
0.3 |
0.7 |
17.0-19.0 |
0.3-1.5 |
0.2 |
0.4 |
CuNi18Zn27 |
2.0742 |
- |
83.5-56.5 |
Solde |
0.3 |
0.5 |
17.0-19.0 |
0.03 |
0.03 |
0.2 |
CuNi25Zn15 |
2.0750 |
Ns6025 |
58.0-61.0 |
Solde |
0.3 |
0.7 |
24.0-26.0 |
0.03 |
0.2 |
0.1 |
|
Retour
haut de page |
Cupro
Nickel |
Désignation |
Composition,
en pourcentage (fourchette ou maxi) |
Symbolique |
|
Ancienne
Designation |
Cu |
Zn |
C |
Fe |
Mn |
Nb |
Ni |
Pb |
S |
Si |
Sn |
Autres
, Total |
Produits
corroyés |
|
2.0862 |
CuNi5Fe |
Solde |
0.5 |
0.05 |
1.0-1.5 |
0.3-0.8 |
- |
4.8--6.0 |
0.03 |
0.05 |
- |
– |
0.1 |
CuNi9Sn2 |
2.0885 |
|
Solde |
0.1 |
- |
0.3 |
0.3 |
- |
8.5-10.5 |
0.03 |
- |
1.8-2.8 |
|
CuNi10Fe1Mn |
2.0872 |
CuNi10Fe |
Solde |
0.5 |
0.05 |
1.0-2.0 |
0.5-1.0 |
- |
9.0-11.0 |
0.03 |
0.05 |
- |
– |
0.3 |
|
2.0878 |
CuNi20Fe |
Solde |
0.5 |
0.05 |
0.5-1.0 |
0.5-1.5 |
- |
20.0-22.0 |
0.03 |
0.05 |
- |
– |
0.1 |
CuNi25 |
2.0830 |
CuNi25 |
Solde |
0.5 |
0.05 |
0.3 |
0.5 |
- |
24.0-26.0 |
0.03 |
0.02 |
- |
– |
0.1 |
CuNi30Mn1Fe |
2.0820 |
CuNi30Fe |
Solde |
0.5 |
0.06 |
0.4-1.0 |
0.5-1.5 |
- |
30.0-32.0 |
0.03 |
0.05 |
- |
– |
0.3 |
CuNi30Fe2Mn2 |
2.0883 |
|
Solde |
0.5 |
0.05 |
1.5-2.5 |
1.5-2.5 |
- |
29-32 |
0.02 |
0.06 |
- |
- |
0.3 |
CuNi44Mn1 |
2.0842 |
CuNi44 |
Solde |
– |
0.05 |
0.2 |
0.5-2.0 |
- |
43.0-45.0 |
0.01 |
0.02 |
- |
– |
0.1 |
Produits
coulés |
G-CuNi10 |
2.0815.01 |
- |
Solde |
0.5 |
- |
1-1.8 |
1-1.5 |
0.15-0.35 |
9-11 |
- |
0.15-0.25 |
- |
0.15 |
G-CuNi30 |
2.0835.01 |
- |
Solde |
0.5 |
- |
0.5-1.5 |
0.6-1.2 |
0.5-1.0 |
29-31 |
- |
0.3-0.7 |
- |
0.15 |
|
Retour haut